1) Bimetal Bar
双金属复合棒
2) bimetal compound
双金属复合
1.
Selecting cast aluminum alloy and cast steel as inner loop and outer loop of the bimetal compound casting respectively, the casting was produced by induction heating in mold.
双金属复合铸件外圈采用铸造铝合金,内圈选取碳素结构钢,采用型内感应加热工艺进行复合。
2.
A good metallurgical combination at interface of bimetal compound casting was obtained.
双金属复合铸件外层采用铸造铝合金,内层选取碳素结构钢,采用型内感应加热工艺进行复合。
3) Bimetallic Cladding Process
双金属复合工艺
4) bimetal composite
双金属复合材料
1.
Study on Interface of High Speed Steel/Structural Steel Bimetal Composite;
高速钢/结构钢双金属复合材料界面研究
2.
Based on the large deformation elastic-plastic finite element method(FEM) theory and finite model,the process of solid phase bonding for Cu/Al bimetal composite by hydrostatic extrusion was analyzed by ANSYS FEM with frictional elements inserted between two contacting metals.
基于大变形弹塑性有限元理论,采用ANSYS有限元程序,通过建立合理的有限元分析模型,对Cu/Al双金属复合材料静液挤压固相结合的非稳态过程进行了数值模拟研究,得到了变形体在挤压过程中的等效应力、应变分布及相对滑动量随摩擦系数的变化情况,揭示了组元金属在静液挤压成形过程中的流动规律,指出在一定的变形量条件下,增大内外层金属之间的摩擦系数是较好实现内外层金属固相结合的主要方法。
3.
So far as the high speed steel-spheroidal graphite cast iron bimetal composite produced by the centrifugal casting and adopted for rollers is concerned,the quality of bimetal binding zone is a main index to evaluate the overall characteristics of product.
对用于轧辊的离心铸造高速钢-球墨铸铁双金属复合材料而言,结合层质量是衡量产品综合性能的主要指标之一。
6) Double iron combined ro11er
双金属复合辊筒
补充资料:双金属、多金属重整
分子式:
CAS号:
性质:采用含有两种或两种以上金属组元重整催化剂的催化重整过程。但反应器可以是固定床也可以是移动床。一般的双金属多指铂和铼,还有铂和锡、铂和铑等;多金属有铂、铼、钛或铂、铱再加上其他金属,这类催化剂活性好可以在较低压力下操作,如铂铼为1.4~1.8MPa,多金属催化剂在移动床甚至可低于0.7MPa。且芳烃转化率高,双金属固定床可达芳潜的120%,而移动床连续重整可达150%~170%。但双金属和多金属催化剂比单铂催化剂对原料中的杂质更敏感。
CAS号:
性质:采用含有两种或两种以上金属组元重整催化剂的催化重整过程。但反应器可以是固定床也可以是移动床。一般的双金属多指铂和铼,还有铂和锡、铂和铑等;多金属有铂、铼、钛或铂、铱再加上其他金属,这类催化剂活性好可以在较低压力下操作,如铂铼为1.4~1.8MPa,多金属催化剂在移动床甚至可低于0.7MPa。且芳烃转化率高,双金属固定床可达芳潜的120%,而移动床连续重整可达150%~170%。但双金属和多金属催化剂比单铂催化剂对原料中的杂质更敏感。