1) waste methanol catalyst
废甲醇催化剂
1.
A process for preparing active ZnO and CuSO4·5H2O from waste methanol catalyst has been developed.
介绍了利用废甲醇催化剂生产活性氧化锌和五水硫酸铜的方法,试验结果表明,最佳工艺条件为:催化剂粒度80目;酸浸反应的硫酸浓度3。
2.
China produces a large amount of waste methanol catalyst each year.
甲醇的产能在所有化工产品中仅次于乙烯和合成氨,每年产生的废甲醇催化剂数量巨大。
2) catalyst
[英]['kætəlɪst] [美]['kætḷɪst]
甲醇催化剂
1.
The experimental study on the source and scathe of the poison sulfur, iron and nickel in methanol catalyst has measured by physical-chemical instruments and chemical analytical methods.
采用电子能谱仪、X光衍射仪、吸附仪等物化仪器和化学分析法,对工业甲醇催化剂使用过程中硫铁镍元素的来源、危害进行实验研究。
3) methanol catalyst
甲醇催化剂
1.
The researches of the optimization of preparation process of methanol catalyst were summarized,also including the increase of catalyst activity and stability by adding the fourth component to the Cu/Zn/AI catalysts,the influence of impurityies on the catalyst properties,as well as the poisoning mechanism,the grain size and the hole structure control of the catalysts,The study on pre-reduction ca.
综述了甲醇催化剂的使用技术及国内外甲醇催化剂的研究进展。
2.
The formation mechanism of iron and nickel carbonyl and their influences on the methanol catalyst are reviewed in detail in this paper.
羰基铁、羰基镍是导致铜基合成甲醇催化剂中毒的物质。
3.
The selection of shift process in industrial produc tion of methanol was discussed, the effecting factors causing the poisoning & loss of activity for methanol catalyst were analyzed from the aspects of chlorine & chloride, metal carbonyl, trace of ammoinia and oil contaminant etc, the appropriate solvable methods were presented.
论述了甲醇工业生产中变换工艺的选择,从氯及氯的化合物、羰基金属化合物、微量氨和油污等方面分析了导致甲醇催化剂中毒失活的影响因素,提出了相应的解决方法。
4) synthesis methanol catalyst
合成甲醇催化剂
1.
Research situation of synthesis methanol catalyst abroad & at home was introduced;the research & development progress of new type of foreign metal catalysts was described for zinc-chromium catalyst,copper base catalyst and alloy catalyst etc.
介绍了国内外合成甲醇催化剂的研究情况;从性能参数、测定数据、制备方法等方面阐述了锌铬催化剂、铜基催化剂、合金催化剂等国外新型金属催化剂的研究进展。
5) Methanol catalyst containing manganese
含锰甲醇催化剂
6) methanol synthesis catalyst
甲醇合成催化剂
1.
Studies on deactivation and regeneration of industrial methanol synthesis catalyst;
工业甲醇合成催化剂的失活与再生研究
2.
Performance and industrial application of NC208, a new methanol synthesis catalyst, is reported.
本文介绍一种NC208型新型甲醇合成催化剂的性能及其工业使用情况。
补充资料：废载体催化剂中铂族金属回收
废载体催化剂中铂族金属回收
recovery of platinum group metal from waste loading catalyst
fe!zaiti euihuaji zhong bozu jinshu huishou废载体催化剂中铂族金属回收(recoveryofplatinum group metal from waste loading eat-alyst)从含铂族金属的废载体催化剂中进行铂族金属再生的过程。催化剂工业是铂族金属的最大用户，含铂族金属废催化剂数量大，需大批量进行工业化回收。废催化剂有载体催化剂和金属催化剂两类，后者按合金度并中铂族金属回收的方法处理。催化剂载体大多数为A1203或Al:03一510:，也有活性炭和有机液等。回收的主要过程是使铂族金属和载体分离，同时得到富集，然后进行精制提纯。回收方法较多，通常采用湿法和火法相互配合的工艺，主要有载体溶解法、铂族金属溶解法、高温氯化法、吸附法、氧化分解法、高温熔炼法、高温焚烧法和机械剥离法等。 载体溶解法用酸或碱溶解载体使铂族金属留在渣中的回收方法。A1203载体多用酸溶，如A1203-0.3%Pt废催化剂，用含硫酸50%的溶液在403~405K温度下浸出lh，A120:以硫酸铝形式进入浸出液，铂族金属残留渣中。过滤后的残渣经缎烧得到含铂12%~18%的缎烧物，铂回收率98.9%。510:载体采用碱溶解，如5102一Auo.2%一Pdo.5%废催化剂，用含NaOHZo%溶液，在NaOH与510:的量比为l:1.5、343~353K温度的条件下溶解5102，铂族金属残留在不溶渣中。不溶渣送把精炼和金精炼，金、把的回收率分别达95%。该法的优点是含铂族金属废催化剂不需要经过预处理，回收流程较短;缺点是化学试剂消耗大，固液分离困难。 铂族金属溶解法一种用溶剂只溶解催化剂中的铂族金属，而少溶解或不溶解载体物质的铂族金属回收方法。为使铂族金属能有效溶解，先烧除催化剂中的积炭和有机物质。缎烧后废催化剂表面的铂族金属处于高度分散状态，比纯金属容易溶解。如A1203一5102-Pto.3%的废催化剂在1173~1423K高温下缎烧4h，使载体中不A1203转变为不溶于酸的。一A1203，然后在含盐酸5~6mol/L溶液和氧化剂存在下加热至沸腾温度浸出3h，铂进入浸出液，浸出率在98.5%以上。浸出液送铂精炼生产纯铂，铂回收率为97%。对载体为510:的含铂族金属废催化剂，可不经预烧直接在盐酸溶液中加入氧化剂进行浸出。如含510:一Auo.2%-Pdo.5%的废催化剂，放在含盐酸1~3mol/L的溶液中加入氧化剂(如NaCIO)，加热至沸腾温度浸出3h，金浸出率98.8肠，把浸出率98.3%，浸出液再分别按金精炼和把精炼方法精制提纯。该法化学试剂消耗少，金属回收率高，生产成本低;缺点是铂族金属仍少量(20~709八)残留渣中需再加回收。