1) microporous aluminosilicates
微孔硅酸铝
2) microporous aluminophosphates
微孔磷酸铝
1.
Some suitable templates are predicted for the formation of microporous aluminophosphates and aluminosilicates molecular sieves with 12-membered ring or 10-membered ring channel structures by analyzing the character of template parameters.
针对微孔磷酸铝和硅铝酸盐两类合成反应体系,通过数据挖掘找出模板剂的参数特征,预测出适用于合成十二元环和十元环微孔磷酸铝和硅铝酸盐的分子筛一系列新的有机胺模板剂。
3) micro-porous calcium silicate
微孔硅酸钙
1.
Flexible micro-porous calcium silicate insulation material is composed of porous spherical agglomerates consisting of many tiny needlelike xonotlite crystals and aluminum silicate fiber,most part of which has been formed flexible ceramic fiber paper before formation of the insulation material.
微孔硅酸钙柔性隔热材料由以硬硅钙石针状微小晶体构成的微孔硅酸钙球形颗粒和硅酸铝纤维复合而成,其中大部分硅酸铝纤维首先形成柔软的纸型材料,微孔硅酸钙颗粒和其余硅酸铝纤维沉积其上,填充在硅酸铝纤维之间的大孔隙中。
2.
Flexible micro-porous calcium silicate(CS/AS),made of micro-porous calcium silicate particles and aluminum silicate fiber by post forming process,has low thermal conductivity.
通过二次成型工艺,以微孔硅酸钙颗粒和硅酸铝陶瓷纤维为主要原料,制成了柔性微孔硅酸钙材料(记为CS/AS),在1000℃时,导热系数为0。
5) Mesoporous silicoaluminophosphate
介孔磷酸硅铝(SAPO)
6) Mesoporous aluminosilicate
介孔硅铝酸盐
补充资料：微孔硅酸钙保温材料
分子式：5GaO·6SiO2·5H2O
CAS号：
性质：为托贝莫来石型绝热材料，耐热度650℃，容量250kg/m3，抗折强度0.3MPa，抗压强度0.5MPa，导热系数0.045W/(m2·K)，线收缩率2％。耐水性好，不腐蚀设备及管道，易加工。由粉状二氧化硅、石灰、纤维增强材料和水经搅拌、凝胶化、成型蒸压和干燥等工序制成。用作设备及管道保温材料和屋面板保温构件。
CAS号：
性质：为托贝莫来石型绝热材料，耐热度650℃，容量250kg/m3，抗折强度0.3MPa，抗压强度0.5MPa，导热系数0.045W/(m2·K)，线收缩率2％。耐水性好，不腐蚀设备及管道，易加工。由粉状二氧化硅、石灰、纤维增强材料和水经搅拌、凝胶化、成型蒸压和干燥等工序制成。用作设备及管道保温材料和屋面板保温构件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。