1) phase interface and temperature characteristics
相界面及温度特性
2) frequency and temperature characteristics
频率及温度特性
3) phase and phase interface
相及相界面
4) phase transformation critical temperature and cooling velocity
相变特征温度及冷速
1.
This paper established a prediction mathematic model for phase transformation critical temperature and cooling velocity of low-alloying structure steel firstly.
本文建立了低合金结构钢CCT曲线特征温度及冷速的预报预测模型,利用TurboC2 编程,实现对不同成分结构钢相变特征温度及冷速较为准确的预报预测,为测定钢CCT曲线时确定温度及冷速提供指导,同时还可以对测量结果进行分析指导及验证。
5) temperature-phase transition properties
温度相变特性
6) interface temperature
界面温度
1.
Results reveal that the interface temperature history decreases sharply at first then approaches to a plateau within the observational time if the thickness of the thin layer is very small (less than 1mm)and the thermal diffusion coefficie.
在三个不同初温、不同热物性参数及边界条件下，获得了夹层介质中的温度解，给出了界面温度历史随薄层厚度、热扩散系数和介质之间热扩散系数之比的变化规律。
2.
The interface temperature and the temperature history near the interface followingthe shock compression are calculated by the method of Cattaneo heat conduction.
冲击压缩后的界面温度和界面附近的温度历史用Ｃａｔｔａｎｅｏ热传导理论作了计算，并与Ｆｏｕｒｉｅｒ热传导理论的结果作了比较。
3.
Trivedi) model and non-equilibrium effect were applied to research the tip radius and interface temperature in order to obtain the transitional characteristic from dendrite to cellular.
结果表明:尖端半径和界面温度均随抽拉速率的增加而减小,到达临界值后又急速增大。
补充资料：界面温度测定
界面温度测定
measurement of temperature in contact interface
1 iemian wendu eeding界面温度$lj定(rneasurement。f temperaturein eontaet interfaee)全属塑性加工过程中工件与工具接触表面之间的温度测定。界面温度影响润滑剂的粘度、反应速率和润滑剂膜的破裂强度，并能以此判断工件通过接触区时的摩擦状态。通常采用动态热偶的方式测定界面温度。下面以全属丝拉拨为例说明测定方法。拉丝模和工件作为热偶的两个组元，将拉丝模与模子支承装置绝缘，形成热偶的一个臂。被拉的金属丝通过模子后被缠绕在卷筒上形成另一臂。用一根导线一端连接到丝材上，一端连接到与卷筒轴相接的水银上。拉丝模作为热点，丝材通过拉模时因发热而产生的电动势由快速响应记录器记录，并换算出界面的温度。在拉拔过程中，丝材冷点到模子之间距离逐渐增加，但这不会影响测量精度。所记录的温度将受到界面膜及可能发生的润滑剂的相互作用的影响，但是拉拔中用的肥皂膜则没有影响。试验表明，只要有足够数量的金属接点存在，就会形成热偶，但表面的氧化物没有影响。在全流体润滑时，这种方法就不能用。 (李小玉)