1) zirconia aqueous slurries
氧化锆水系料浆
1.
Aqueous slurries of 8%(mol fraction) yttriastablized zirconia were firstly prepared Measurements and analytical methods to zeta potential, rheological properties, sediment experiment, SEM photographs of sediment particles were used for optimizing parameters High dispersible and stable zirconia aqueous slurries are gained through adjusting pH value and dispersant content
选用8%(摩尔分数)氧化钇稳定氧化锆粉,制成氧化锆水系料浆。
2) zirconia slurry
氧化锆浆料
4) zirconia gas sensitive ceramic
氧化锆系气敏材料
5) hydrous zirconia
水合氧化锆
1.
A series of hydrous zirconia samples were prepared by the hydrothermal method,and the Pt/WO3-ZrO2 catalyst was prepared by impregnation.
通过水热法合成了一系列水合氧化锆,以之为载体采用浸渍法制备了Pt/WO3-ZrO2催化剂,考察了氢氧化锆的水热温度对Pt/WO3-ZrO2异构化活性的影响。
6) aluminium oxide and zirconia system
氧化铝-氧化锆系
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。