1) direct carburation
直接碳化法
2) direct carbonization
直接碳化
1.
Ultrafine WC powders prepared by direct carbonization process and the structure and properties of its cemented carbide;
新型直接碳化法制备超细WC粉及其烧结体的结构与性能
3) phosgenation method polycarbonate
直接光气化法聚碳酸酯
4) CDRM
碳粉直接还原法
5) direct reduction & carbonization
直接还原碳化
1.
While the Co3O4,transition-metal oxides(V2O5,Ta2O5,MoO3 and TiO2) and carbon black was the raw materials,ultrafine Co-inhibitor composite powders(Co-VC,Co-TaC,Co-Mo2C and Co-TiC),which can be applied in hardmetal industry,were synthesized via direct reduction & carbonization process in vacuum.
以氧化钴(Co3O4)、过渡金属氧化物(V2O5、Ta2O5、MoO3、TiO2)和碳粉(C)为原料,用真空直接还原碳化技术制备了应用于硬质合金的钴-抑制剂(Co-VC、Co-TaC、Co-Mo2C、Co-TiC)超细复合粉末。
2.
Nano-composite WC-Co powder was synthesized by direct reduction & carbonization process.
用直接还原碳化法制备了纳米复合WC-Co粉末。
6) esterification
[英][e,sterifi'keiʃən] [美][ɛ,stɛrəfə'keʃən]
直接酯化法
1.
Five long-chain saturated alkanoyl-6O-D-isoascorbates(alkanoyl=decanoyl,lauroyl,myristoyl,palmitoyl and stearoyl) were synthesized by esterification(or transesterification) of D-isoascorbic acid with alkanoic acids using concentrated H_2SO_4 as a medium and a catalyst at room temperature.
用浓H2SO4作为反应介质和催化剂,通过直接酯化法或酯交换法合成了5个D-异抗坏血酸脂肪酸(癸酸,月桂酸,豆蔻酸,棕榈酸和硬脂酸)酯,其结构经1H NMR和IR表征。
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。