1) non-equilibrium segregation of boron
硼的非平衡偏聚
1.
The non-equilibrium segregation of boron in matrix grains was indirectly revealed in high boron (1.
运用电子显微分析手段 ,将经过循环热处理的Fe Cr B合金晶粒中的二次析出相与经过常规热处理晶粒中的二次析出相加以比较 ,直接揭示了在高含硼的Fe Cr B合金的基体中出现的硼的非平衡偏聚现象 研究发现 ,在晶粒中硼的非平衡偏聚的产生与加热温度、奥氏体相、奥氏体化后的冷却速度和循环热处理的次数有
2) non equilibrium segregation of phosphor
磷的非平衡偏聚
3) Non-Equilibrium Segregation
非平衡偏聚
1.
The non-equilibrium segregation of boron on grain boundaries experienced three stages when the samples were cooled from 1150℃ to 640℃ at 2 ℃ /s, and transformed to boron precipitates at 860℃ .
采用硼（Ｂ）径迹照相法和透射电镜从实验上观察了连续冷却过程中Ｂ在晶界非平衡偏聚的发生发展过程。
2.
Grain boundary non-equilibrium segregation phenomenon has been found in many alloysystems.
溶质晶界非平衡偏聚现象已在大量合金系中发现。
3.
This phenomenon could only be explained by diffusion of vacancy-Si complex inducing non-equilibrium segregation.
这种偏聚只能用空位-Si原子复合体扩散导致的非平衡偏聚理论来解释。
4) non-equilibrium grain boundary segregation
非平衡偏聚
5) non-equilibrium grain-boundary segregation
非平衡晶界偏聚
1.
The dynamic curve of non-equilibrium grain-boundary segregation and the impact temperature curve for 2.
25Cr1Mo和12Cr1MoV钢式样的非平衡晶界偏聚动力学曲线以及冲击温度曲线。
6) non-equilibrium segregation
非平衡晶界偏聚
1.
By solution treatment,isothermal aging treatmenmt and impact test, the critical time t_(c) for non-equilibrium segregation of residual element Tin in 0.
通过固溶处理和等温时效处理及冲击试验等简单方法,确定出连续冷却过程中残留元素Sn在低碳钢中发生的非平衡晶界偏聚及在不同温度下的临界时间tc。