1) vanadium oxide thin film
氧化钒薄膜
1.
Study on pulse laser damage of vanadium oxide thin film;
氧化钒薄膜脉冲激光损伤研究
2.
Study on Process of Vanadium Oxide Thin Films for Uncooled Infrared Deterctors;
非致冷红外探测器用氧化钒薄膜工艺研究
3.
The vanadium oxide thin films have been prepared by R.
利用射频磁控溅射的方法,在不同的衬底温度和溅射功率下制备了氧化钒薄膜样品,并在纯氩气环境下作了退火处理,用X射线衍射(XRD)、X射线光电子能谱(XPS)和激光扫描共聚焦显微镜扫描图像,对样品进行研究。
2) vanadium oxide thin films
氧化钒薄膜
1.
Study on preparation and electrical properties of vanadium oxide thin films by an organic Sol-gel process;
氧化钒薄膜的有机溶胶—凝胶制备及电学性能研究
2.
In order to study the application of vanadium oxide thin films in the uncooled IR microbolometer, the factors of effects on the thermally sensitive properties of vanadium oxide thin films are summarized, and the mechanism is researched into.
为研究氧化钒薄膜在非致冷红外微测辐射热计中的应用,综述了制备工艺等诸多因素对氧化钒热敏特性的影响,对其机理进行了探究,结果表明掺杂和新的制备工艺是调整氧化钒热敏特性较为有效的方法。
3) vanadium oxide films
氧化钒薄膜
1.
Ti-and Al-doped vanadium oxide films were deposited using magnetron co-sputtering techniques on quartz substrates.
以石英片为基底材料,采用直流/射频磁控共溅射方法制备了掺Al和掺Ti的氧化钒薄膜,重点探索了用这种方法制备掺杂氧化钒薄膜的工艺条件,对所制备的氧化钒薄膜进行了热光性能测试,并利用能带理论对测试结果进行分析。
4) Vanadium dioxide thin film
氧化钒薄膜
1.
In this paper, we present the fabrication and the electrical characteristics of Vanadium dioxide thin film which is used in un-cooled infrared bolometric arrays.
氧化钒薄膜是优异的热敏材料,在许多技术领域中具有广阔的应用前景,已成为国内外功能材料研究的热点之一。
5) Vanadium
[英][və'neɪdiəm] [美][və'nedɪəm]
氧化钒薄膜
1.
In this paper, several thin films samples of Vanadium oxide were got by high-frequency Magnetron sputter with pure metal vanadium as sputter source.
本文以高纯金属钒作为靶材，采用磁控溅射工艺制备氧化钒薄膜。
2.
In this paper, Several thin films samples of Vanadium oxide were got by Vacuum vapor by pure V2O5 power as vapor source and high-frequency Magnetron sputter by high pure metal vanadium.
本文分别采用高纯五氧化二钒和高纯金属钒作为源和靶材，采用真空镀膜工艺，并通过正交试验设计优化了真空蒸发工艺和磁控溅射工艺制备氧化钒薄膜的实验过程，在实验中着重改变了对薄膜特性影响很大的几个工艺条件，如：功率、基片温度，O_2/Ar比例等。
补充资料：硅-氧化钠-五氧化二钒系湿敏材料
分子式：
CAS号：
性质：一种感湿体材料。主晶相为硅粉，氧化钠和五氧化二钒起助熔体和黏结作用。680℃固相烧结法制取。游离硅粒保证瓷体的低电阻率，氧化钠和五氧化二钒有利于吸收水分，受潮后使硅粒之间的电阻值显著下降。材料响应速度慢，吸湿时间≥5min，脱湿时间≥l0min，宜用于中湿和湿度变化不太快的场合。制作的湿敏元件体积小、机械强度好、阻值范围可调，工作寿命长。
CAS号：
性质：一种感湿体材料。主晶相为硅粉，氧化钠和五氧化二钒起助熔体和黏结作用。680℃固相烧结法制取。游离硅粒保证瓷体的低电阻率，氧化钠和五氧化二钒有利于吸收水分，受潮后使硅粒之间的电阻值显著下降。材料响应速度慢，吸湿时间≥5min，脱湿时间≥l0min，宜用于中湿和湿度变化不太快的场合。制作的湿敏元件体积小、机械强度好、阻值范围可调，工作寿命长。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条