1) Polythionic acid corrosion
连多硫酸腐蚀
1.
The reason of cracking in elbow of the hot hi-pressure segregator oil P3327 pipeline in the hydrocracking unit was analyzed and a method to prevent from polythionic acid corrosion was provided.
对国产加氢裂化热高分油管线的弯头开裂原因进行了分析 ,并对预防连多硫酸腐蚀提出了相应的防范措
3) PSCC
连多硫酸应力腐蚀开裂
1.
Stress Corrosion Cracking of polythionic acids(PSCC) of 304 SS were investigated by SSRT,SEM and metallographic analysis.
采用慢应变速率拉伸试验(SSRT)、扫描电镜断口分析以及金相显微组织分析等方法对304不锈钢连多硫酸应力腐蚀开裂(PSCC)行为进行了研究。
4) polythionic acid stress corrosion cracking
连多硫酸应力腐蚀破裂
6) sulfate resistance
硫酸盐腐蚀
1.
Research methods:The performances of concrete with the anticorrosive mixture were investigated in the experiments, such as concrete chloride diffusivity, sulfate resistance and drying/wetting cycle in corrosive environments, etc.
研究方法:通过混凝土离子渗透性试验、硫酸盐腐蚀试验、干湿腐蚀循环试验等对耐腐蚀辅料的性能进行了测试,并对该耐腐蚀混凝土辅料的耐腐蚀机理进行了分析。
补充资料：连多硫酸应力腐蚀破裂
分子式：
CAS号：
性质：奥氏体不锈钢应力腐蚀破裂的一种类型。主要发生在接触高温含硫介质的化工装置中。在高温下钢表面生成硫化铁，当装置停车时温度降低，硫化铁与水分和空气相接触，反应生成连多硫酸H2SxO6(x=3，4，5)，导致不锈钢发生晶间型应力腐蚀破裂。抗晶间腐蚀性能较好的钢种，其抗连多硫酸应力腐蚀破裂的性能也较好。
CAS号：
性质：奥氏体不锈钢应力腐蚀破裂的一种类型。主要发生在接触高温含硫介质的化工装置中。在高温下钢表面生成硫化铁，当装置停车时温度降低，硫化铁与水分和空气相接触，反应生成连多硫酸H2SxO6(x=3，4，5)，导致不锈钢发生晶间型应力腐蚀破裂。抗晶间腐蚀性能较好的钢种，其抗连多硫酸应力腐蚀破裂的性能也较好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。