1) Cu-Cr-Zn/γ-Al_2O_3
Cu-Cr-Zn/γ-Al2O3
1.
A series of copper based catalysts are prepared and Cu-Cr-Zn/γ-Al_2O_3 is chosen as a catalyst finally.
制备了一系列的铜基催化剂用于此反应,筛选得到了Cu-Cr-Zn/γ-Al2O3催化剂,在最佳反应条件下,乙醇的转化率达93%,N-乙基哌嗪的选择性达90%以上;而且在100 h的寿命实验中,N-乙基哌嗪的选择性保持在86%以上。
2) Cu-Zn/γ-Al2O3(Co)catalyst
Cu-Zn/γ-Al2O3(Co)催化剂
3) Cu Cr/γ-Al_2O_3 catalyst
Cu Cr/γ-Al_2O_3
4) Cu-Zn-Cr alloy
Cu-Zn-Cr合金
1.
The effects of different heat-treatment process on Cu-Zn-Cr alloy s hardness are studied.
文章通过不同的热处理工艺来研究固溶时效对Cu-Zn-Cr合金硬度的影响。
2.
Cu-Zn-Cr alloy was prepared by Ingot Metallurgy.
发现，Cu-Zn-Cr合金的强化机制包括固溶强化、形变强化及析出强化。
3.
The results show that: The first,Cu-Zn-Cr alloy is .
Cu-Zn-Cr合金是典型的时效强化型合金。
5) Cu/ZrO_2/S_2O~(2-)_8/γ-Al_2O_3
Cu/ZrO2/S2O82-/γ-Al2O3
1.
Cu/ZrO_2/S_2O~(2-)_8/γ-Al_2O_3 solid acid catalyst was prepared by loading of(NH_4)_2S_2O_8,ZrOCl_2 and Cu(NO_3)_2 onto γ-Al_2O_3 step by step,which was obtained from calcining of pseudoboehmite.
考察了Cu/ZrO2/S2O82-/γ-Al2O3在富氧条件下对C3H6选择还原NO的催化性能,并借助SEM、XRD、Py-IR和TPR等表征方法研究了它的结构和性能的关系。
6) Cu-ZnO-Al_2O_3/HZSM-5
Cu-Zn-O-Al2O3/HZSM-5
补充资料：Cu-Zn-Al shape memory alloy
分子式：
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。