1)  molten slag
熔融炉渣
1.
According to physics-chemistry character of molten slag, on the basis of production experience of blast furnace Smelting Lead, the paper describe the way of lowering Lead containing in Lead blast furnace slag.
分析了熔融炉渣的物理化学性质,在认真总结鼓风炉炼铅生产实践经验的基础上,指出降低铅鼓风炉炉渣含铅的途径。
2)  melting
熔融
1.
Mechanical property,melting and crystallization behaviors of toughened PA1010;
增韧PA1010的力学性能及熔融与结晶行为
2.
Study of Melting of Extrudate by Twin-screw Extruder;
双螺杆挤出机物料熔融因素的研究
3.
Study on decreasing ash-melting temperature of Lu'an coal with spent F-T catalyst and economic analysis of it;
F-T废催化剂降低潞安煤煤灰熔融温度的试验研究及其经济性探讨
3)  melt
熔融
1.
Study on melting characteristics of MSWI fly ash;
垃圾焚烧飞灰的熔融特性研究
2.
Problems existed in production of compound fertilizer by urea melt spheroidizing process and its countermeasures;
尿素熔融喷浆造粒生产复合肥有关问题的探讨
3.
Howevee,some harmful substance volatilized from fly ash in melting process,which caused second contamination.
熔融固化处理是安全的处理方法,但飞灰熔融过程中有有害物质挥发,造成二次污染。
4)  fusion
熔融
1.
The effect of extension on fusion and crystallization of PA1010/6;
拉伸对PA1010/6熔融和结晶的影响
2.
The influence of coal ash compositions upon fusion and slagging properties is comparatively complex.
煤灰中化学成分对煤灰的熔融和结渣特性的影响比较复杂。
3.
A method for the determination of WO_(3) in wolfram ore and Cr_(2)O_(3) in chromite by XRF with sample preparation of high-dilution fusion glass-disc was developed.
用X射线荧光光谱测定钨砂中WO3和铬铁矿中Cr2O3,通过高倍稀释熔融玻璃片制样法,采用高纯WO3或Cr2O3作单一标准样测量X射线荧光强度计数,然后同未知样品测量所得X射线荧光强度计数相比,即可计算出WO3和Cr2O3的测量值。
5)  Molten salt
熔融盐
1.
Study on gasification characteristics of waste printed circuit boards (PCB) in molten salts;
废弃印刷线路板熔融盐气化特性研究
2.
Investigation of LiNiO_2 as cathode material for lithium ion battery synthesized by a molten salt method;
熔融盐法合成锂离子电池正极材料LiNiO_2的研究
3.
Electrodeposition of aluminum from AlCl_3-NaCl-KCl molten salt;
AlCl_3-NaCl-KCl熔融盐中铝的电沉积
6)  vitrification
熔融固化
1.
To investigate the characteristic of heavy metal during the vitrification of municipal solid waste incineration (MSWI) fly ash, a pilot scale experiment was carried out to treat MSWI fly ash from a MSWI plant in Hangzhou City using a diesel oil furnace for more than 6 months.
为探索垃圾焚烧飞灰中重金属在熔融过程中的迁移特性,采用燃油式表面熔融炉,对杭州某生活垃圾焚烧厂的焚烧飞灰连续进行了6个多月日处理规模为500kg/d的熔融固化中试实验。
参考词条
补充资料：熔融炉渣的分子假说
    　　把熔融炉渣看成是各种氧化物分子（如CaO、FeO、SiO2等）及它们之间的化合物分子(如2CaO·SiO2、2FeO·SiO2等)所组成的理想溶液的假说。 在处理熔渣-钢液二相间的冶金反应平衡问题时，这种假说认为只有"自由"的氧化物才能参加反应，而且认为质量作用定律以其理想的形式适用于熔渣-钢液二相间反应申克(H.Schenck)最早用这种观点说明炼钢过程反应。奇普曼(J.Chipman)学派早年用这种观点处理氧在熔渣- 钢液二相间分配与脱磷反应，为使"平衡常数"守常，他们曾假定了熔渣中有诸如(2CaO·SiO2)2、(CaO·SiO2)2等无法证明其存在的化合物"双分子"，从而导致这种假说本身的内在的自相矛盾。对熔融炉渣的电化学性质的研究结果已经证明，它是离子溶液而不是"分子"溶液。
　　
　　分子假说把冶金反应写成分子形式，例如脱硫反应，即熔渣中的（CaO）和钢液中的［FeS］反应：
　　
(CaO)＋[FeS]─→(CaS)＋[FeO]

常能简明并定性地说明熔渣组成对反应平衡移动的影响，所以一些冶金书刊中至今仍有沿用这种写法的，但这并不意味着熔融炉渣是由各种"分子"构成的。
　　

说明：补充资料仅用于学习参考，请勿用于其它任何用途。