1) Critical thermal shock temperature difference
临界热震温差
2) critical temperature difference
临界温差
1.
Based on the critical stress fracture criterion and by means of the calculation of the time for the surface of the functionally gradient ceramie plate to attain its local fracture strength, the expression of the critical temperature difference △Tc leading to the critical t.
基于陶瓷材料的临界应力断裂判据,通过求解无限大对称型梯度功能陶瓷平板表面达到其局部断裂强度的时间,建立了引起其表面临界热应力的临界温差ΔT_c的表达式,并以此作为对称型梯度功能陶瓷的抗热震参数。
2.
The critical temperature differences (ΔTC) of various sample thicknesses are obtained, which shows that the critical temperature differences decrease gradually with the increasing plate thick.
通过实验研究了ZrB2-20%SiC-10%AlN(ZSA)超高温陶瓷基复合材料的热物理性能、力学性能和其热冲击开裂过程,确定了不同厚度试样热冲击开裂的临界温差;随着试样厚度的增加,热冲击开裂的临界温差逐渐降低。
3) critical temperature difference(△T_c)
临界温差(△T_C)
4) critical temperature difference
临界温度差
5) thermal critical point
热临界点,临界温度
6) critical preheat temperature
临界预热温度
1.
On the basis of the result of the Y-slit crack test,the critical preheat temperature and critical cooling time(t_(8/5cr)) of JG590 under the condition of different heat input and welding material were determined by theoretic computation.
采用插销实验、斜y形坡口焊接裂纹实验和焊接热影响区最高硬度实验对厚度30 mm的JG590钢板的焊接冷裂纹敏感性进行了研究,分析了插销试件的断口和显微组织,以斜y形坡口焊接裂纹实验结果为基础,通过理论计算得到了JG590钢在不同焊接线能量、不同焊接材料情况下的临界预热温度和临界冷却时间。
补充资料:水热温差法
分子式:
CAS号:
性质:利用高温高压状态下矿物的溶解度与温度成正比这一现象而进行人工合成晶体的方法。其原理为:当溶液的浓度一定时,在一定的温度和压力条件下,矿物的溶解度也一定(饱和状态)。当温度由t1降成t2时,由于高温高压状态下矿物的溶解度与温度成正比,因此相应地溶解度m2<m1,溶液呈过饱和状态,由结晶学理论可知,将有m1-m2的物质结晶出来。目前此法广泛地运用于水晶、冰洲石、石榴石和萤石等晶体的合成。
CAS号:
性质:利用高温高压状态下矿物的溶解度与温度成正比这一现象而进行人工合成晶体的方法。其原理为:当溶液的浓度一定时,在一定的温度和压力条件下,矿物的溶解度也一定(饱和状态)。当温度由t1降成t2时,由于高温高压状态下矿物的溶解度与温度成正比,因此相应地溶解度m2<m1,溶液呈过饱和状态,由结晶学理论可知,将有m1-m2的物质结晶出来。目前此法广泛地运用于水晶、冰洲石、石榴石和萤石等晶体的合成。