1)  roll welding
轧焊
2)  Weld Point (line)
轧焊点(线)
3)  hot roll welding
热轧焊
4)  ARB
累积叠轧焊
1.
Microstructure and Bonding Interface of TA1/Q235 Clade Plate Manufactured by ARB Process;
累积叠轧焊制备钛钢复合板的组织与结合界面
5)  accumulative roll-bonding
累积叠轧焊
1.
Study on microstructure and mechanical properties evolution of pure Aluminum produced by accumulative roll-bonding process;
纯铝累积叠轧焊组织与性能演变规律研究
2.
Improvment of the quality and mechanical properties of a plain carbon steel by accumulative roll-bonding;
累积叠轧焊工艺改善普碳钢材料性能特征
6)  vacuum hot roll bonding
真空热轧焊接
1.
This article describes a study of the application of a vacuum hot roll bonding technique to Ti alloy plate and stainless steel plate using the composite interlayer of copper(pure copper and copper contains lanthanon Yt) and Nb sheet.
采用铜(纯铜及含稀土元素钇的铜)+铌的复合中间层进行了钛合金与不锈钢板的真空热轧焊接试验,测试了接头拉伸强度,并利用金相显微镜、扫描电镜、XRD、能谱对连接界面的微观结构、断口形貌及中间层材料铜的组织进行了分析,结果表明,连接界面结合良好,无未焊合或开裂处;焊后未生成金属间化合物,在铌-钛合金界面处存在一厚度约为2。
参考词条
补充资料:激光焊与氩弧焊的修模具的区别
激光焊与握弧焊是常用的模具修复的两种方法。

氩弧焊
氩弧焊是电弧焊的一种,利用连续送进的焊丝与工件之间燃烧的电弧作热源,由焊炬喷嘴喷出的气体保护电弧来进行焊接的。目前氩弧焊是常用的方法,可适用于大部分主要金属,包括碳钢、合金钢。熔化极惰性气体保护焊适用于不锈钢、铝、镁、铜、钛、锆及镍合金,由于价格低,被广泛用于模具修复焊,但焊接热影响面积大、焊点大等缺点,目前在精密模具修补方面已逐步补激光焊所代替。

激光焊
激光焊是高能束焊的一种,激光焊是利用大功率相干单色光子流聚焦而成的激光束为热源进行的焊接。这种焊接方法通常有连续功率激光焊和脉冲功率激光焊。 激光焊优点是不需要在真空中进行,缺点则是穿透力不如电子束焊强。激光焊时能进行精确的能量控制,因而可以实现精密器件的焊接。它能应用于很多金属,特别是能解决一些难焊金属及异种金属的焊接。目前已广范用于模具的修复。

修复模具时的主要区别

使用非消耗电极与保护气体,常用来焊接薄工件,但焊接速度较慢,且热输入比激光焊大很多,易产生变形,激光焊焊缝的特点是热影响区范围小,焊缝较窄,焊缝冷却速快、,焊缝金属性能变化小,焊缝较硬。

精密模具的焊接不同于其他零件焊接,其对质量控制的要求非常严格,而且工件的修复周期必须越短越好。 传统的氩焊发热影响区大,对焊接周边造成下塌,变形等几率非常高,对于精度要求高,焊接面积大的模具,必须经过加温预热,在特定温度下进行焊接,还要自然降温进行退火处理,如此折腾下来费用和时间都不能为用户所接受;而冷焊又存在焊接不牢固和脱落等缺陷。而激光焊没有氩焊和冷焊这些不足,因此逐渐被广泛应用。