1) centerline shrinkage
中心缩松
1.
Sensitivity factor of centerline shrinkage (SFCS), which is the criterion for shrinkage formation in slab, is put forward based on solidification theory, numerical simulation, experimental investigation and mathematical deduction.
连铸坯内部中心缩松、缩孔是影响铸坯内部质量的主要缺陷之一。
2) shrinkage porosity
缩松,松心
3) central porosity
中心疏松
1.
On the industrial experiments the effect of electromagnetic stirring on central porosity,equiaxial crystal ratio,shrinkage cavities and surface quality as well as effect of electromagnetic stirring on the solidification of the continuous casting billet have been analyzed and discussed.
根据工业试验结果,分析了结晶器电磁搅拌(M-EMS)对马氏体不锈钢连铸坯的中心疏松、等轴晶率、缩孔及表面质量的影响,并对电磁搅拌对铸坯凝固的影响机理进行了探讨。
2.
At the present production conditions,the results of trials showed that centerline segregation and central porosity are improved.
对结晶器电磁搅拌改善大方坯质量进行了工业性对比试验,并对电磁搅拌参数进行了优化,在现有的工艺条件下,达到了改善铸坯中心偏析和中心疏松的目的。
4) center porosity
中心疏松
1.
The reasons of center porosity,shrinkage cavities and surface quality in CC bloom of Martensite stainless steel have been analyzed and the effect of Mould-Electromagnetic Stirring and other factors on center porosity,shrinkage cavities and surface quality has been investigated.
对马氏体不锈钢方坯中心疏松、缩孔及表面凹陷的成因作了分析,探讨了电磁搅拌等对减少中心疏松、缩孔及表面凹陷的作用,并根据攀长钢公司的具体情况提出了预防措施。
2.
The results show that application of appropriate electromagnetic stirring parameters can improve the macrostructure of austenitic stainless steel,in which both columnar grains and equiaxed grains are evidently refined and center porosity and shrinkage cavity can be remarkably decreased,and enlarging equiaxed grains zone.
在工业实验中研究了低频电磁场对水平连铸奥氏体不锈钢组织的影响,结果表明:在低频电磁场作用下,合适的电磁搅拌参数使奥氏体不锈钢宏观组织在一定程度上得到了明显改善,铸坯的柱状晶和等轴晶得到了显著的细化,消除了穿晶现象,等轴晶区扩大,中心缩孔、中心疏松级别明显降低;多次实验发现:对于奥氏体不锈钢,所需的搅拌强度应高于一般钢种,即使搅拌器的中心磁感应强度达900GS平均值(幅值达到1413GS),采用3～4Hz的频率,搅拌后对钢液的组织影响较小;在同样的磁场强度下,不锈钢液由于粘度大,因而其转速比碳钢液的转速约低20%～30%。
3.
Center segregation and center porosity will seriously affect the internal slab quality for continuous casting bloom.
连铸过程中出现的铸坯中心偏析和中心疏松会严重影响铸坯内部质量。
5) central pipe
中心缩孔
1.
The updated mathematic models for calculation of the central pipe formotion in continuous cast billet are built up, based on the material balance and the previous published models.
通过物质平衡原理讨论并新建立了计算方坯中心缩孔的数学模型。
6) shrinkage center
收缩中心
1.
In order to gain a clear idea of the shrinking direction of injection molding products,the shrinkage mechanism is analyzed and,thereby,a concept of shrinkage center is derived.
本文针对注塑模具设计中存在的注塑制品收缩方向含混不清的问题 ,通过分析注塑成型制品的收缩机理 ,提出“收缩中心”的概念 ,建立能够对实际收缩情况进行合理解释的收缩规则 ,并据此开发了预测注塑成型制品收缩率分布趋势的程序 ,计算结果与实验结果吻合较好。
补充资料：氟西缩松
分子式：
CAS号：
性质：又称氟西奈德，氟西缩松，肤轻松，氟去炎舒松。白色或近白色结晶性粉末，无味。熔点265～266℃。不溶于水，易溶于丙酮，在乙醇、氯仿中溶解，在乙醚中微溶。以16,17-环氧黄体酮为原料制得。本品为外用皮质激素中疗效最显著而副作用较小的一种，对皮肤、黏膜炎症、瘙痒及皮肤过敏反应等均有效。适用于湿疹、神经性皮炎、皮肤瘙痒症、接触性皮炎、牛皮癣、盘状红斑狼疮、扁平苔癣、日光性皮炎等。制剂有乳膏，油膏，洗剂。
CAS号：
性质：又称氟西奈德，氟西缩松，肤轻松，氟去炎舒松。白色或近白色结晶性粉末，无味。熔点265～266℃。不溶于水，易溶于丙酮，在乙醇、氯仿中溶解，在乙醚中微溶。以16,17-环氧黄体酮为原料制得。本品为外用皮质激素中疗效最显著而副作用较小的一种，对皮肤、黏膜炎症、瘙痒及皮肤过敏反应等均有效。适用于湿疹、神经性皮炎、皮肤瘙痒症、接触性皮炎、牛皮癣、盘状红斑狼疮、扁平苔癣、日光性皮炎等。制剂有乳膏，油膏，洗剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条