1) Roasting-oxidation leaching
焙烧氧化浸出
2) chlorinate-roast-leach
氯化焙烧浸出
1.
94% and the recovery of chlorinate-roast-leach was 82.
试验考察了盐酸、硝酸、硫酸以及盐酸加助溶剂浸出钪时各因素的影响和浸出效果,以及氯化焙烧浸出、碱熔合浸出的浸出效果。
4) Oxidizing roasting
氧化焙烧
1.
The phase transformation and weight loss rate of ludwigite in oxidizing roasting were studied by DTA-TG,isothermal TG and XRD.
利用DTA-TG、恒温TG和XRD测试方法研究了硼铁矿氧化焙烧过程中的相变和失重率。
2.
The arsenolite cinders were treated by the processes of oxidizing roasting-pyrolusite pulp absorption,magnetizing roasting-magnetic separation and acid leaching.
采用氧化焙烧—软锰矿浆吸收、磁化焙烧—磁选、酸浸工艺处理砷华废渣。
3.
Germanium is recovered from gerichened vacuumn furnace slag of Shaoguan smelter using the flowsheet of ball milling neural leaching oxidizing roasting chloridizing distillation hydrolysis.
针对韶冶真空炉提锌产生的富锗渣 ,提出了“球磨 中性浸出 氧化焙烧 氯化蒸馏 水解”工艺回收其中的锗。
5) oxidation roasting
氧化焙烧
1.
Based on a great deal of researches for recovery of S, Fe and Zn from solid waste, a comprehensive utilization technique, including oxidation roasting-absorptio.
本文综述了从固体废渣中回收利用S、Fe、Zn的大量研究成果,同时考虑到原料来源、处理技术、经济效益等因素,采用氧化焙烧-软锰矿浆吸收、磁化焙烧-磁选、酸浸的方案实现砷华生产废渣的综合利用,并通过进一步的试验探索了设计方案的各项优化工艺参数。
2.
The effects of temperature,time,air frequency and different fluxes on the recovery rate of molybdenum for oxidation roasting on low grade molybdenum ore are discussed.
实验研究了低品位钼精矿在氧化焙烧过程中温度、时间、通氧气次数、不同熔剂对钼的氧化转化率的影响。
3.
Oxidation roasting was a pretreatment technique for low-grade and complex siderite, the parameters of oxidation roasting were important to roasting efficiency.
氧化焙烧是解决低品位复杂难选菱铁矿的有效前处理工艺,氧化焙烧参数对焙烧效果影响很大。
6) oxidation roast
氧化焙烧
1.
This paper presents that Cr,Si and Al in raw materials of magnetic cobalt-alloy are removed by oxidation roast method using NaNO 3and Na 2CO 3which are chemicals commonly adopted,and they are directly decomposed by H 2SO 4,since a technique combined to extraction is botained.
论述了使用常用化工原料NaNO3、Na2 CO3 进行氧化焙烧法除去磁钴合金料中的Cr、Si、Al,并直接用H2 SO4分解 ,从而得到与萃取除杂联接的工
2.
Oxidation roast test of iran's Mo concentrate in a rotary tube electric furnacehas revealed that physical and chemical properties of the concentrate has a great effect on itsoxidation roast performance, and in order to obtain satisfactory cinder from this type concentrate proper measures must be taken during roasting.
通过回转管电炉焙烧伊朗钼精矿的工艺试验,发现该矿的一些理化指标对其氧化焙烧过程具有很大影响。
补充资料:氧化浸出
氧化浸出
oxidizing leaching
yanghuaJ一nehu氧化浸出(oxidizing leaehing)加入氧化剂使矿石、精矿或其他固体物料中的有价组分在浸出过程中发生以氧化反应为特征的浸出方法。工业上常用的氧化剂有空气、氧、Fe3+、MnO:和el:等。 对金属或低价金属氧化物而言,氧化浸出的目的是使金属氧化为离子或使低价离子氧化为易溶性高价离子进入溶液。前者如含金、银矿石的氰化物浸出: ZAu+4CN一+02+ ZHZO= ZAu(CN)牙+ZOH一+2H2O2 ZAg+SCN一+02十ZHZO=ZAg(CN)牙+4OH-浸出过程中元素金和银分别被空气中的氧氧化并与CN一络合呈配位离子形态进入溶液;后者可举含U02为主的铀矿氧化酸浸出为例: ZFe3++UOZ=UO鑫++ZFeZ+此时,氧化剂为Fe3+。为避免Fe3+反应生成的UO呈十发生水解沉淀,浸出过程必须在酸性介质中进行。硫化矿物的氧化浸出与含金、银矿石氰化物浸出及铀矿氧化酸浸出的情况不同,前者浸出过程发生氧化反应的主要是硫。例如,硫化锌精矿的氧压酸浸出反应可表示为: ZnS+ZH++1/202=ZnZ++HZO+50 ZnS+202=ZnZ++50泛-实践证明,硫的氧化产物主要为元素硫。其他硫化矿物的常压或加压氧化酸浸,硫的氧化产物也主要是元素硫。回收得到的元素硫便于贮存和运输,这是硫化矿物氧化浸出的主要优点。