1) formed squeeze head
成形触头
1.
A kind of new experimental molding machine, air impact experimental molding machine with formed squeeze head pushed by air fluid was designed and manufactured.
设计并研制了一种新型的气冲造型实验机—气冲气推成形触头压实造型实验机。
2) bridge shaped contact
桥形触头
1.
In order to reduce contacting resistance of bridge shaped contact and lower down temperature rise,improvement design was carried out for DW450-1100 universal circuit breaker bridge shaped structure.
为减小桥形触头的接触电阻,降低温升,对DW450-1600万能式断路器的桥形触头结构进行了改进设计。
3) wedge contact
楔形触头
4) knife contact
刀形触头
5) thixoforming
触变成形
1.
Numerical Simulation of Thixoforming for High Solid Fraction Semi-solid Magnesium Alloy;
高固相率半固态镁合金触变成形数值模拟
2.
Numerical simulationin of semi-solid AZ91D magnesium alloy thixoforming;
AZ91D镁合金半固态触变成形的数值模拟
3.
Algorithm Optimization of Gating System Parameters of Semi-solid Alloy Thixoforming;
半固态触变成形浇注系统基本参数的算法优化
6) Thixo-forming
触变成形
1.
Preparation and Thixo-forming Characteristics of Mg-Al-Zn Semi-solid Alloy Billets;
Mg-Al-Zn合金半固态坯的制备及触变成形研究
2.
Die-casting process of semi-solid thixo-forming of AZ91D Mg alloy;
AZ91D镁合金半固态触变成形压铸工艺
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。