1) GaP nanocrystals
GaP纳米晶
1.
Synthesis of GaP nanocrystals by elemental reactions under solvothermal conditions;
溶剂热条件下单质直接反应合成GaP纳米晶
2.
GaP nanocrystals were synthesized by high temperature high pressure beuzene ther-inal synthesis method, the samples were charartrized by X-ray cliffraction,optical absorption and transmission election microscope.
用高温高压苯热合成方法制备了GaP纳米晶，用X射线衍射、光吸收谱及透射电子显微镜对所得样品进行了分析测试。
2) GaP-nanoparticles
纳米GaP
3) GaP nanoparticles
纳米GaP粉体
1.
Three kinds of dispersant were used to disperse GaP nanoparticles.
采用三种不同类型的分散剂对纳米磷化镓(GaP)粉体进行分散,并用测量滤液吸光度的方法来比较分散效果;测定了纳米GaP粉体的等电点,以及采用十二烷基苯磺酸钠分散时的Zeta电位,并初步制备了纳米GaP/聚乙烯吡咯烷酮(PVP)复合薄膜。
4) GaP/Morin nanocomposite
GaP/桑色素纳米复合材料
1.
The GaP/Morin nanocomposites were synthesized by ultrasonic irradiation.
采用超声波辐射法制备了不同桑色素量的GaP/桑色素纳米复合材料 ,研究了其形态及可能的形成机理 。
5) nanocrystalline
纳米晶体
1.
Study on preparation and structural characteristics of ZnFe_2O_4 nanocrystalline;
铁酸锌纳米晶体的制备及表面光伏特性研究
2.
Electrodeposition of nanocrystalline Fe-Ni-Cr alloy foil in trivalent chromium bath;
三价铬镀液中电沉积纳米晶体Fe-Ni-Cr合金箔
3.
Synthesis of nanocrystalline nickel by direct current electrodeposition;
直流电沉积法制备纳米晶体镍
6) KZnF_3 nanoparticles
KZnF_3纳米晶
补充资料：maximum experimental safety gap
分子式：
CAS号：
性质：在规定试验条件下，两个经长25mm的间隙连通的容器，一个容器内燃爆时不致引起另一个容器内燃爆的最大连通间隙。中国规定气体、蒸气危险物质按最大试验安全间隙分为ⅡA级，ⅡB级和ⅡC级。甲烷(I类爆炸危险物质)的最大试验安全间隙为1.14mm。最大试验安全间隙≤1.14mm，>0.0mm的为ⅡA级；≤0.9mm，>0.5mm的为ⅡB级；≤0.5mm的为ⅡC级。气体、蒸气危险物质按最小点燃电流比和最大试验安全间隙都分为ⅡA，ⅡB和ⅡC级，但其结果只是近似相符。
CAS号：
性质：在规定试验条件下，两个经长25mm的间隙连通的容器，一个容器内燃爆时不致引起另一个容器内燃爆的最大连通间隙。中国规定气体、蒸气危险物质按最大试验安全间隙分为ⅡA级，ⅡB级和ⅡC级。甲烷(I类爆炸危险物质)的最大试验安全间隙为1.14mm。最大试验安全间隙≤1.14mm，>0.0mm的为ⅡA级；≤0.9mm，>0.5mm的为ⅡB级；≤0.5mm的为ⅡC级。气体、蒸气危险物质按最小点燃电流比和最大试验安全间隙都分为ⅡA，ⅡB和ⅡC级，但其结果只是近似相符。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条