1) the amount of gas evolution from the coating
涂料发气量
1.
The effects of the component of coating,like refractory filler, adhesive and suspension-agent on the amount of gas evolution from the coating, resistance to high temperature and suspension-ability of coating etc.
试验结果表明 ,只要涂料发气量≤ 3ml/g ,铸钢管就不会产生气体缺
2) coating pick-up
涂料涂附量
3) air-drying coatings
气干涂料
4) pneumatic dispensing
气动涂料
5) luminous paint
发光涂料
1.
The waterborne luminous paint for interior wall is prepared with self-made styrene-acrylate emulsion as binder, covered luminous particles as filler and other additives.
以自制的苯丙乳液为基料,加入包覆处理过的发光颜料和其它助剂制备成水性内墙发光涂料,并对其性能进行了测试和表征。
2.
By researching the luminescence of SrAl_2O_4:Eu,Dy long afterglow luminous paint,the conclusion was obtained that the influence of the coating matrix to SrAl_2O_4:Eu,Dy long afterglow luminous paint was not so obvious.
通过对SrAl2O4:Eu,Dy长余辉发光涂料进行发光学研究,得出涂料母体对SrAl2O4:Eu,Dy长余辉发光粉的发光不存在明显影响的结论,同时利用二级e指数衰减公式研究了长余辉发光涂料的发光动力学,并测得其快衰减寿命和慢衰减寿命的数值。
3.
The methods to prepare polyester acrylate resin and SrAl_(2)O_(4):Eu~(2+) luminous materials were investigated with respect to the climate resistance,acid and alkali resistance,oil- proof ability,corrosion resistance,mechanical properties,and intensity and lasting time of persistent luminescence of the luminous paint made of the same.
为了提高发光涂料的耐候性、耐酸碱性、耐油性、耐腐蚀性和力学性能以及余辉强度和余辉时间,对聚酯丙烯酸树脂和铝酸锶铕发光材料的制备方法进行了研究,并将发光材料分散于聚酯丙烯酸树脂中,制备出了高性能的发光涂料。
6) luminescent coatings
发光涂料
1.
Through a orthogonal test with 3 facrors and a number of comparison tests,a optimum composition for fluorescent pigment based luminescent coatings has been obtained:acrylic resin 40%～45%,calcium carbonate 30%～35%,organic luminescent pigment 20%～25%,and the rest toluene,defoamer,and plasticizer.
利用 3因素 4水平正交试验和一系列对比试验 ,得到了荧光颜料型发光涂料最佳配比组成 :丙烯酸树脂4 0 %～ 4 5 %、碳酸钙 30 %～ 35 %、有机发光颜料 2 0 %～ 2 5 %、甲苯、消泡剂和增塑剂等适量。
2.
3 types of oil-based luminescent coatings were prepared by mixing SrAl2O4∶Eu2+,Dy3+ and Sr4Al14O25∶Eu2+,Dy3+ with long afterglow luminescent powders into nitryl/alkyd varnish and nitryl white plaint,with the aid of dispersants and defoaming agent.
采用市售SrAl2O4∶Eu2+,Dy3+和自制Sr4Al14O25∶Eu2+,Dy3+两种长余辉发光粉分别与硝基白漆、硝基清漆和醇酸清漆混合,在分散剂和消泡剂等助剂的作用下制备了3种油性长余辉发光涂料。
3.
The researching advancement at home and abroad, advantages and disadvantages, applied field of the light-retaining luminescent coatings, and the species of the coatings include sulphide system, alkaline earth metal aluminate system and silicate system etc were reviewed.
综述了硫化物、碱土金属铝酸盐、硅酸盐等系列的蓄光型自发光涂料的国内外研究进展、优缺点和应用领域。
补充资料：非占位涂料(转移涂料)
4.1 概 述 非占位涂料又称转移涂料,其工作原理是将涂料直接喷涂到芯盒或模样表面,然后填砂、紧实,涂料层和型(芯)砂在芯盒的约束下同时固化,起模时涂料能从芯盒或模样表面转移到砂型(芯)表面,从而制得带有涂料的精密砂型(芯)。由于这种工艺方法所形成的涂层不占据型腔的有效位置,故称为非占位涂料法,亦称转移涂料法。采用这种方法不会影响型(芯)的尺寸精度,涂层可完美地复制出模样或芯盒的表面,不存在刷痕、流淌、堆积等涂料表面缺陷,能获得精密光洁的铸件,可与熔模铸造相媲美,而其成本仅相当于或略高于普通砂型铸造,生产效率大大提高。 4.2 国内外的研究应用情况 非占位涂料技术最早是出现在20世纪70年代,是日本小松制作所提出的小松(Komatsu)—山西(Yamanishi)法,简称K-Y法。该法的工艺过程为,首先在喷涂有分型剂并已预热的金属芯盒上涂敷粉状涂料,然后加入树脂覆膜砂,加热固化后由顶杆将壳型顶出。在壳型上,涂料已由芯盒内表面转移到树脂覆膜砂壳型表面形成了光洁的铸型表面。此法采用的粉状涂料和所能制造的型(芯)形状都受限制,所以难以推广。
80年代初,小松制作所对原来的Ｋ-Ｙ法进行了改进,发展成为有机系新Ｋ-Ｙ法。新Ｋ-Ｙ法的工艺流程如图1,先在环氧树脂玻璃钢芯盒表面涂衬上硅橡胶膜,然后将涂料液倒入芯盒中,使涂料润湿整个芯盒内表面后,再倒出多余的涂料,在芯盒表面留下一层涂料;在振动条件下,向涂敷涂料层的芯盒内充填芯砂,再送入微波炉内加热,使涂料与覆膜砂一起硬化,然后脱芯盒,取出带有涂料的精密砂芯。新Ｋ-Ｙ法有许多优点:芯盒本身不受热,尺寸稳定,有利于提高砂芯的精度和延长芯盒的使用寿命;由于填砂是在室温下进行的,所以不必非得用树脂覆膜砂,可以直接填加粉状树脂和原砂的混合料;又由于使用的是液态涂料,可以很方便地涂挂在各种形状的芯盒或模样各个角落,所以对芯子的形状几乎没有限制。
1987年日本又开发了无机系的新Ｋ-Ｙ法。所用芯砂为水玻璃覆膜砂,即先将无机系水基涂料涂敷在芯盒或模样表面,再充填包覆有水玻璃等无机粘结剂的干态砂,经微波照射,涂料中介质损失系数大的水分被选择加热,变成水蒸汽向芯盒外逃逸,此时,水蒸汽可将包覆在砂粒表面的无机粘结剂再次溶解,进而又干燥硬化,制得带有涂料的无机系精密砂芯。目前日本对Ｋ-Ｙ法研究较多,已有Ｋ-Ｙ法的专用涂料和芯盒制作的专利，并已形成机械化生产线。有机系的新Ｋ-Ｙ法已被用来制造柴油机汽缸盖、进气道、排气道芯子及某些建筑零件。无机系的新Ｋ-Ｙ法也已被用来生产叶轮、导叶、气缸盖、涡轮机匣、三角刃刀头等铸件,取得了良好的效果。