1) vanadium-microalloying
V微合金化
1.
The strengthening and toughing mechanism of vanadium-microalloying steel and the technological trait of CSP line are reviewed.
分析了V微合金化钢的强韧化机理及CSP生产线的工艺特点,探讨了V微合金化技术在CSP生产线应用的可行性和应注意的主要问题。
2.
The effect of vanadium-microalloying and controlled rolling & controlled cooling technique was investigated.
为在CSP线利用V微合金化加控制轧制生产550MPa以上高强度HSLA钢,通过试验钢的成分设计、模拟CSP连铸、试验轧制和Gleeble试验,初步确定了该产品在CSP线的生产工艺,为下一步深入研究CSP线的V微合金化行为奠定了基础。
2) V-N microalloying
V-N微合金化
1.
The V-N microalloying obviously increased mechanical properties of steel 16MnV(N) with σ_b=520～625MPa,σ_s=395～465MPa,δ_5=24%～28%,and A_K=43～96J.
对V-N微合金化提高低合金结构钢强韧性的机理进行了研究。
2.
In this paper the effect of V-N microalloying on section homogeneiey of mechanical properties of H beam is studied.
针对高强度厚壁H型钢易在截面不同部位产生性能差异的特点,研究了V-N微合金化方式对高强度厚壁H型钢性能均匀性的影响。
3.
Producing practice shows that using Si3N4-alloy to conduct V-N microalloying can reduce the amount of Fe-V by about 55% without reducing the mechanical properties of HRB400 III steel compared with single Fe-V adding.
分析碳化硅铁用于生产含V HRB400 III级钢的机理,生产的实践表明,常规轧制的HRB400 III级钢,在保证力学性能不降低的条件下,添加氮化硅铁的V-N微合金化比单纯加入钒铁的V微合金化HRB400 III级钢的钒铁加入量减少55%,经济效益明显。
3) V-N microalloyed
V-N微合金化
1.
In this paper, the production and propening parameter of V-N microalloyed HRB400 rebar is introduced.
本文介绍了首钢V-N微合金化HRB400钢筋的生产与技术性能指标,分析了V-N微合金化后钢中的N的变化情况和存在形式,对HRB400钢筋的晶粒大小与HRB335钢筋做了对比,介绍了钢筋的使用性能,对使用HRB400钢筋做了技术经济分析,使用HRB400钢筋每吨钢可节约230元以上。
5) Nb-V Microalloying
Nb-V微合金化
1.
An Analysis on Surface Cracks Formation of H Beam of Nb-V Microalloying Steel BS55C;
Nb-V微合金化H型钢BS55C表面裂纹成因分析
6) V microalloyed steel
V微合金化钢