1) poly(hexane-sebacate)
聚癸二酸己二醇酯
1.
High molecular weight biodegradable poly(hexane-sebacate) was synthesized by direct polycondensation from sebacic acid and 1,6-hexanediol, the chemical structure was identified by FT-IR and ()~1H-NMR, the intrinsic viscosity was measured by Ubbelohde viscometer, the melting point, glass transition temperature was determined by DSC, and the tensile strength is (23.
以癸二酸和己二醇为原料,以十氢萘为溶剂,进行直接聚合,合成了高分子量聚癸二酸己二醇酯,产率达到96%。
2) polyhexamethylene adipate glycol
聚己二酸己二醇酯二醇
1.
Water borne polyurethane coating for wood was prepared from toluene diisocyanate, polyhexamethylene adipate glycol and dimethanol propionic acid.
以甲苯二异氰酸酯 (TDI)、聚己二酸己二醇酯二醇 (PHA)、二羟甲基丙酸 (DMPA)等为原料 ,采用内乳化法制备了水性聚氨酯 ,研究了NCO与OH摩尔比、PHA相对分子质量及交联剂三羟甲基丙烷用量对水性聚氨酯成膜物性能的影响。
3) Adipic acid, 1,3-butylene glycol polymer, isodecyl alcohol modified
己二酸与1,3-丁二醇异癸酯的聚合物
4) Polyglycol adipate
聚二醇己二酸酯
5) Adipic acid, 1,6-hexanediol polymer
聚(1,6-己二醇己二酸酯-1,6己二醇-己二酸)
6) polybutylene glyool adipate
聚己二酸丁二醇酯二醇
补充资料：1,10-癸二醇
分子式：C10H22O2
分子量：174.28
CAS号：112-47-0
性质：白色针状结晶。熔点72-75℃，沸点192℃（2.67kPa），170℃（1.07kPa）。易溶于醇和热乙醚，几乎不溶于冷水和石油醚。
制备方法：由癸二酸经酯化、还原而得。1.酯化将癸二酸、乙醇、苯、对甲苯磺酸加入装有水分离器的反应锅中，加热回流，带水约4-5h，至无水分分出为止，冷却过滤，得癸二酸二乙酯粗品。收率85%。2.还原先将癸二酸二乙酯及无水乙醇投入反应锅中，在搅拌及冷却下再将金属钠逐渐加入，加热回流到金属钠全部溶解，无残留物为止。进行水蒸汽蒸馏，回收乙醇，然后再加入水稀释，冷却，析出的粗品用苯重结晶即得成品，收率为54%。
用途：医药中间体。
分子量：174.28
CAS号：112-47-0
性质：白色针状结晶。熔点72-75℃，沸点192℃（2.67kPa），170℃（1.07kPa）。易溶于醇和热乙醚，几乎不溶于冷水和石油醚。
制备方法：由癸二酸经酯化、还原而得。1.酯化将癸二酸、乙醇、苯、对甲苯磺酸加入装有水分离器的反应锅中，加热回流，带水约4-5h，至无水分分出为止，冷却过滤，得癸二酸二乙酯粗品。收率85%。2.还原先将癸二酸二乙酯及无水乙醇投入反应锅中，在搅拌及冷却下再将金属钠逐渐加入，加热回流到金属钠全部溶解，无残留物为止。进行水蒸汽蒸馏，回收乙醇，然后再加入水稀释，冷却，析出的粗品用苯重结晶即得成品，收率为54%。
用途：医药中间体。