1) Alloy compound
合金化合物
2) gold compound
金化合物
3) alloy nitride
合金氮化物
4) metal compound
金属化合物
1.
Reaction properties of H-ZSM-5 zeolite catalysts modified by alkali-earth and rare-earth metal compounds;
碱土和稀土金属化合物对H-ZSM-5沸石催化剂改性的反应性能
2.
The effect of metal compounds and carbon black on the afterglowing characteristic of HIPS and PE-LD was studied, the possible mechanism of afterglowing was explored.
采用锥形量热仪研究了金属化合物、还原性物质等添加剂对HIPS及PE-LD阴燃特性的影响,以及炭黑等填料在阴燃中的作用,并且对阴燃机理作了初步探索。
3.
This paper has probed into the regulation of alloy phase formation,according to exist phase diagrams and metal compounds in R-(Cu,Ni) binary and terary system.
根据Ｒ－（Ｃｕ，Ｎｉ）二元和三元体系的相图及其所存在的金属化合物，探讨了这些体系的相形成规律。
5) metallic compound
金属化合物
1.
This paper studied the synergism effect between IFR and metallic compounds.
探讨了几种金属化合物对PP膨胀阻燃体系的影响,通过锥形量热仪分析了体系的阻燃性,SEM观察燃烧后材料的成炭情况。
2.
Stimulative effects of metallic compounds on industrial sewage sludge combustion and the sludge with acid washing treatment were studied by thermogravimetric analysis.
用热重法研究了不同金属化合物对含工业污水污泥的助燃作用,计算了添加不同金属化合物前后污泥燃烧的特征指数和燃烧反应动力学参数,并以酸洗污泥作为对比,对不同金属化合物的助燃效果和催化机制进行了分析。
3.
This paper studied the synergism effect between IFR and metallic compounds.
研究了几种金属化合物对PE-HD膨胀阻燃体系(IFR)的协同作用,通过极限氧指数(LOI)、DSC-TG、SEM对复合材料的阻燃、热稳定性和成炭情况进行研究,分析了金属化合物与膨胀阻燃剂协效作用机理。
6) alloy carbide
合金碳化物
1.
The surface microstructure is fine needle-covered martensite and dispersed alloy carbides which result in high hardness.
结果表明 ,激光淬火时 ,当表层区所需能量密度为 4 0J/mm2 时 ,表面硬度最高 ,组织为隐针马氏体和弥散分布的合金碳化物 ;过渡区由于发生托氏体转变 ,硬度明显下降。
2.
The surface microstructure is fine cryptocrystalline martensite and alloy carbide which results in high hardness.
结果表明 ,表面激光淬火时 ,当表层区所需能量为 30J/mm2 时 ,硬度值最高 ;表层组织为细小、隐晶马氏体和弥散分布大小不一的合金碳化物 ,硬度很高 ;过渡区由于托氏体的析出 ,硬度明显下降 ,这种显微组织使冲头耐磨性、抗冲击性都提高 ,也延长了其使用寿
3.
In this paper, the relation between the type, quantity and distribution of alloy carbides precipitated during tempering and toughness of 21/4Cr1Mo steel is studied, and the toughening mechanism of 21/4Cr1Mo steel is discussed
用相分析手段研究了２１４Ｃｒ－１Ｍｏ钢回火过程中合金碳化物类型、含量、分布等与韧性的关系，并对其韧化机制进行了探讨。
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜