1) CF/PPEK
碳纤维增强杂萘联苯聚醚酮
1.
In this paper pre-impregnated hot compression molding process of the CF/PPEK and CF/PPES unidirectional compound plates were studied and mechanical properties of prepared unidirectional composites were discussed by experiment.
本文研究了碳纤维增强杂萘联苯聚醚酮(CF/PPEK)和碳纤维增强杂萘联苯聚醚砜(CF/PPES)2 种 复合材料单向板的预浸热压成型工艺,对制备的单向板进行了力学性能试验研究,并利用 X 射线光电子能 谱(XPS)和扫描电子显微镜(SEM)对这两种复合材料的界面状态和结构进行了分析。
2) CF/PPES
碳纤维增强杂萘联苯聚醚砜
1.
In this paper pre-impregnated hot compression molding process of the CF/PPEK and CF/PPES unidirectional compound plates were studied and mechanical properties of prepared unidirectional composites were discussed by experiment.
本文研究了碳纤维增强杂萘联苯聚醚酮(CF/PPEK)和碳纤维增强杂萘联苯聚醚砜(CF/PPES)2 种 复合材料单向板的预浸热压成型工艺,对制备的单向板进行了力学性能试验研究,并利用 X 射线光电子能 谱(XPS)和扫描电子显微镜(SEM)对这两种复合材料的界面状态和结构进行了分析。
3) carbon fibers reinforced polyetheretherketone(CFR/PEEK)
碳纤维增强聚醚醚酮
1.
The surface tension of comparison of titanium alloy,polyetheretherketone(PEEK),and carbon fibers reinforced polyetheretherketone(CFR/PEEK)
钛合金、聚醚醚酮(PEEK)和碳纤维增强聚醚醚酮(CFR/PEEK)~*表面张力的比较
5) PPESK
杂萘联苯聚醚砜酮
1.
The effect of additives-PVPK30 and Tween80 on the structure and performance of PPESK hollow fiber ultrafiltration membranes was studied.
通过考察添加剂—聚乙烯吡咯烷酮(PVPK30)和Tween80对杂萘联苯聚醚砜酮(PPESK)中空纤维超滤膜结构和分离性能的影响,发现:随高分子添加剂聚乙烯吡咯烷酮K30浓度的升高,膜水通量减小,截留率基本无变化,膜结构逐渐由指状结构转变成海绵状结构。
2.
The effects of additives——PEG600 and oxalic acid on the structure and performance of PPESK hollow fiber ultrafiltration membranes were studied.
通过考察添加剂PEG600和草酸对杂萘联苯聚醚砜酮(PPESK)中空纤维超滤膜结构和分离性能的影响,发现:PEG600的加入不会改变膜的内部结构,均为指状结构,随着PEG600浓度的增加,膜致密层厚度逐渐增加。
3.
A random-arranged experimental design method has been used to study the structure and performance of poly(phthalazine ether sulfone ketone)(PPESK)membranes.
以杂萘联苯聚醚砜酮/聚乙烯吡咯烷酮/N-甲基吡咯烷酮(PPESK/PVP/NMP)为铸膜液体系,对杂萘联苯聚醚砜酮的膜结构进行了计算机直接试验设计。
6) sulfonated poly(pathalazinone ether ketone)
磺化杂萘联苯聚醚酮
1.
Zirconium tricarboxybutylphosphonate/sulfonated poly(pathalazinone ether ketone)composite proton exchange membrane for DMFC;
直接甲醇燃料电池用三羧基丁烷膦酸锆/磺化杂萘联苯聚醚酮复合质子交换膜
补充资料：聚杂环纤维
分子式：
CAS号：
性质：由大分子主链含杂环的聚合物纺制成的合成纤维。如聚苯并咪唑纤维(PDI)、聚双苯并咪唑-苯并菲绕啉纤维(BBB)、聚酰胺亚胺纤维(Kermel)、聚酰亚胺纤维(PRD-14)、聚亚苯基噁二唑纤维(POD-Z)等。纤维有很好耐热性和耐热辐射性，短期使用温度400～600℃，正常使用温度-150～340℃，分解温度560～700℃，零强度温度560～750℃。纤维有很好的阻燃性。一般以湿法、干法和干-湿法纺丝成形。主要用作高温绝缘材料和输送带，绝热幕，防护用品，特殊工作服和宇航制品。
CAS号：
性质：由大分子主链含杂环的聚合物纺制成的合成纤维。如聚苯并咪唑纤维(PDI)、聚双苯并咪唑-苯并菲绕啉纤维(BBB)、聚酰胺亚胺纤维(Kermel)、聚酰亚胺纤维(PRD-14)、聚亚苯基噁二唑纤维(POD-Z)等。纤维有很好耐热性和耐热辐射性，短期使用温度400～600℃，正常使用温度-150～340℃，分解温度560～700℃，零强度温度560～750℃。纤维有很好的阻燃性。一般以湿法、干法和干-湿法纺丝成形。主要用作高温绝缘材料和输送带，绝热幕，防护用品，特殊工作服和宇航制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条