1) WO 3 bulk
WO3块材
1.
We report here that the nanostructured WO 3 bulk has an obvious electrochromic effect, which does not exist in ordinary WO 3 bulk.
实验发现纳米WO3块材具有明显的常规块材不具有的电致变色特性 ,即当样品中有电流通过时 ,样品从负极到正极颜色由黄色变为深蓝色 。
2) tungsten oxide
WO3
1.
Nano structured tungsten oxide films have been prepared using a sol-gel process with the starting tungsten powders together with the spin coating method in this paper.
报道了以钨粉为原料,采用溶胶 凝胶技术和旋转镀膜方法,制备出了气致变色WO3纳米薄膜。
2.
Nano powder tungsten oxide is prepared by using a sol-gel process with oxalic acid and benzoic acid as coagulator.
采用溶胶—凝胶法分别用草酸和苯甲酸为凝胶剂制得纳米WO3粉体。
3) WO_3
WO3
1.
The mesoporous WO_3 film was prepared by the solgel-pyrolysis method with the PEG-400 as the structure-directing agent.
采用溶胶-凝胶-热解工艺,以PEG-400为结构导向模板剂,合成出介孔WO3薄膜,通过XRD、SEM、BET等对其晶相组成,显微结构,比表面积和孔径分布等进行了测试,结果表明所制备的介孔WO3薄膜材料为立方晶相,其平均孔径在6。
2.
A series of WO_3 catalysts were obtained through pyrolysis of ammonium paratungstate under different O_2/Ar at 700℃.
在不同组成O2/Ar混合气体条件下,于700℃将仲钨酸铵加热分解制备WO3催化剂。
3.
WO_3 nano-powder was prepared by CTAB/butarol/butane/H_2O microemulsion system with microemulsion method, and the structure, size and topography of WO_3 nano-powder were characterized with X-ray diffractometer, transmissive electron microscopy.
采用CTAB/正丁醇/正辛烷/水微乳体系制备了纳米WO3粉体,并用X射线衍射仪、透射电子显微镜对WO3粉体进行了表征,研究含水量、煅烧温度对WO3粉体的物相结构、粒径大小和形貌的影响。
4) tungsten trioxide
WO3
1.
Under the optimal conditions that n ( cyclohexanol) ∶n ( hydrogen peroxide)∶n ( tungsten trioxide) was 100∶600∶4,the reaction temperature was 100℃ and the reaction time was 6 h,the isolated yield of adipic acid could reach 67.
以WO3为催化剂,H2O2氧化环己醇合成己二酸。
2.
when n(cyclohexanone)∶n(hydrogen peroxide)∶n(tungsten trioxide) was 100∶500∶2,and the reaction temperature was 120 ℃,the reaction time was 6 h,the isolated yield of .
以WO3为催化剂,在无有机溶剂和相转移催化剂的情况下,用H2O2氧化环己酮合成己二酸。
3.
The effect of the preparation process on particle size, specific surface area, crystal form and crystalline morphology of the tungsten trioxide was investigated by TEM and XRD etc.
以仲钨酸铵(APT)为原料,通过正交设计和单水平实验,采用水热法处理制备了WO3粉体。
5) WO 3
WO3
1.
Discolor treatment of chemical fiber wastewater was studied using WO 3 as catalyst in this paper.
以WO3粉体作为催化剂对化纤厂废水采用光催化氧化法进行脱色处理,讨论了光催化氧化法的反应机理,以及化纤厂废水的pH值、光催化剂的投入量、光照时间各因素对废水色度去除率的影响。
2.
WO 3-PEO electrochromic thin films are prepared by sol-gel method,and the method of orthod experiment design,and the effects o f dopping PEO on the electrochromic properties of WO 3 thin films have been st udied by using electrochemical cycling Voltampere.
通过溶胶 -凝胶方法 ,采用正交设计试验研究制备出了掺杂 PEO的 WO3电致变色薄膜 ,并利用电化学循环伏安装置、分光光度计、X- Ray衍射进行了相关的性能测试 ,指出掺杂一定量的 PEO可使氧化钨薄膜离子、电子传导率加快 ,薄膜响应速度加快 ,同时也使薄膜的变色性能提
3.
WO 3 electrochromic thin films were grown by low voltage reactive ion plating on glass and plastic substrates.
在电子束蒸发镀膜的基础上 ,引入低压反应离子镀工艺制备WO3 电致变色薄膜 ,研究不同氧分压对WO3 薄膜电致变色特性的影响 ,实验结果表明制备时选择工作气体氩气分压为 2× 10 -2 Pa,氧分压为 4× 10 -2 Pa时 ,薄膜具有最好的电致变色特性和最大的变色范围。
6) WO3-based gas-sensing material
WO3基气敏材料
补充资料：高温超导体块材组织结构
高温超导体块材组织结构
microstructure of the bulk high temperature superconductor
高温超导体块材组织结构mierostrueture of thebulk high temPerature supereonduetor高温超导体的相组成、晶粒形貌和尺寸，以及与超导电性关系密切的冶金缺陷和晶体缺陷。块材是指薄膜和纤维之外的三维大尺寸材料。 1986年以来陆续发现的高临界转变温度Tc超导体是一个具有陶瓷特性的庞大家族。除Tc高之外，还有很多不同于传统低Tc超导体的共同特征:它们大多具u)为化学全部有超;即的多二uo犷望，叮类。晶块为片和铺这些质相卜、杂和原常常1988Zn)、薄膜约晶Cu、杂相 贫a一b超流角为:值。在相目肠样密度匀单靠实有畸变的层状钙钦矿结晶结构;成分多是以铜((主要元素的金属氧化物，氧含量和含铜材料中铜跳价态都具有不确定性;化合物中大多数金属元素司或部分被其他金属元素替代而不明显改变或仍然具导电性;晶体结构和超导电性具有明显的各向异性使在同一种超导体中，往往共生着结构和Tc各异种超导相。BISrCaCuO(BSCCO)、YBa((YBCO)和TIBaCaCuO(TBCCO)系最有实用矛而被研究得最多的是BSCCO和YBCO超导体。 块材晶粒排列从组织形态上块材可分以下了①晶粒随机取向多晶块:晶轴取向呈无规排列的多材。又称颗粒超导体。秘(Bi)系多晶块中的晶粒状，c轴平行于片的厚度方向;忆(Y)、锭(TD(La)系块材晶粒形状类似，为等轴或棒状晶。在多晶材料中，往往含有少量的非超导金属氧化物杂和孔洞。体密度为理论密度的70一95%。晶粒尺二相和孔洞所占的体积分数和分布状态，与制作工艺始粉末粒度、坯料的成分均匀度有关。在晶界附近，可观察到由热加工过程中应力集聚产生的微裂纹。年和1990年，美国的D.拉巴勒斯蒂(LarbalestiD.戴莫斯(Dimos)等人先后分别对忆系烧结块和双晶作了深入的研究。在烧结块中，有75%以上界是清洁无杂相的，其余不到25%的晶界为含富贫Y、贫钡(Ba)和氧(O)的杂相薄层;即使是无的晶界，其两侧snln的短程区也是富Cu、贫BaO的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条