1) SCR forming
SCR成形
1.
It is shown that the strong shearing and heat disturbance action of SCR forming process on alloy melt affect the behavior of migration of free crystal TiC and the dis.
利用SCR成形技术,使液固反应法获得的Al 5Ti 0。
2) selective catalytic reduction
SCR
1.
Kinetics study of the selective catalytic reduction of NO with NH_3 over V_2O_5-WO_3/TiO_2 catalyst;
V_2O_5-WO_3/TiO_2催化剂氨法SCR脱硝反应动力学研究
2.
The selective catalytic reduction(SCR) of NOx which is the most efficient technology hasn' t been widely used due to its high cost.
在我国燃煤电站中,大多采用低NOx燃烧技术,而脱硝效率较高的选择性催化还原(SCR)技术则应用较少。
3.
Based on the actual flue gas denitrification project in Suizhong Power Plant,the process of Selective Catalytic Reduction(SCR) denitrification technology were introduced.
以绥中发电B厂的烟气脱硝工程为例,介绍了选择性催化还原(SCR)脱硝工艺,并对SCR脱硝系统对锅炉设备的影响进行了分析,提出了解决对策,为新建脱硝系统及脱硝装置改造提供借鉴。
3) CH_4-SCR
CH4-SCR
4) SCR method
SCR法
1.
It is reported in this paper that NOx's create of ceramic kiln and it's pollution to environment were Analyzed, method of reduce NOX of ceramic kiln by adopt SCR method was discussed.
本文根据陶瓷窑炉的特定燃烧环境,分析了NOx的生成以及对环境的危害,探讨了采用选择性催化还原法--SCR法 降低陶瓷窑炉中NOx方法。
5) inter-lock
SCR段
6) Urea-Selective Catalytic Reduction
urea-SCR
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。