1) quaternary ammonium cellulose nitrate
季铵型硝化纤维素
1.
The quaternary ammonium cellulose nitrate(QACN) was prepared by reacting cellulose nitrate(with degree of subtitution 1.
15 )与 3 氯 2 羟基丙基三甲基氯化铵 (CHPA)反应合成了一种新的硝酸酯基取代度为 1 0 3、季铵基取代度为 0 38的季铵型硝化纤维素吸附剂 (QACN)。
3) quaternary ammonium type hemicellulose
季铵型半纤维素
5) nitrocellulose
[英]['naitrəu'seljuləus] [美][,naɪtro'sɛljə,los]
硝化纤维素
1.
Relationship between Viscosity and Concentration of Nitrocellulose;
硝化纤维素在稀溶液中粘度与浓度的依赖关系
2.
The Viscosity Behaviour of Nitrocellulose Chain in Freezing Procedure;
硝化纤维素溶液冰冻过程中的粘度行为
3.
The title alkyd resin modified waterborne nitrocellulose emulsion was prepared by alkyd resin phase inversion process.
采用醇酸树脂相反转乳化法制备了硝化纤维素乳液。
6) Cellulose nitrate
硝化纤维素
1.
The cellulose nitrate containing secondary amine group(ACN) was prepared by one-pot method in two steps: etherification and amination.
以硝化纤维素为原料 ,经一锅法醚化和胺化 2步反应合成了仲胺型硝化纤维素 (ACN)。
补充资料：硝化纤维素
硝酸纤维素实际上是纤维素的硝酸酯，它是以精制短棉绒为原料，用硝酸、硫酸的混合酸进行酯化，使纤维素中的-OH基酯化成－ONO2的产物。根据纤维素中3个-OH基酯化程度的不同，就可得到不同含氮量的CN，随着酯化程度增大，台氮量升高，三硝酸纤维素的理论含氮量为14．14％。不同含氮量的硝酸纤维素有着不同的溶解度和用途。塑料用的含氮量为10．5-12．3％，胶粘剂和涂料用的为11．5％-12．2％，火药用的为11．8％-13．5％。硝酸纤维素的聚合度n＝100-3500，分子量为16200-875000。
CN为白色或微黄色絮绒状固体，无臭、易燃 、易爆，相对密度1.58-1.65，熔点160-170 ℃，闪点12．78℃，自燃温度170℃，折射率1．51。不溶于水，易溶于酮、酯、醇、醚类溶剂，硝酸纤维素对碱很敏感，容易发生皂化而脱硝。长期在光和热作用下能分解并降低含氮量。
硝酸纤维素主要用于配制溶剂型胶桔剂，粘接赛璐珞塑料制品和火药。配制火棉胶。
由于硝化纤维素性质很不稳定，易燃易爆，当温度超过40 ℃时能加速分解而发生自燃。含水25％时较安全，因此在贮运时加入30％左右的乙醇或水为湿润剂，以增加稳定性。使用前应将硝酸纤维素的水烘干，要特别注意安全、最好使用水烘箱，如果用电烘箱温控一定要可取，烘箱门不得关死，防止爆炸。中间观察时人不得面对烘箱开门，以防发生意外。
贮存于阴凉、通风的专用库房内，温度不超过30℃，远离火种和热源。
CN为白色或微黄色絮绒状固体，无臭、易燃 、易爆，相对密度1.58-1.65，熔点160-170 ℃，闪点12．78℃，自燃温度170℃，折射率1．51。不溶于水，易溶于酮、酯、醇、醚类溶剂，硝酸纤维素对碱很敏感，容易发生皂化而脱硝。长期在光和热作用下能分解并降低含氮量。
硝酸纤维素主要用于配制溶剂型胶桔剂，粘接赛璐珞塑料制品和火药。配制火棉胶。
由于硝化纤维素性质很不稳定，易燃易爆，当温度超过40 ℃时能加速分解而发生自燃。含水25％时较安全，因此在贮运时加入30％左右的乙醇或水为湿润剂，以增加稳定性。使用前应将硝酸纤维素的水烘干，要特别注意安全、最好使用水烘箱，如果用电烘箱温控一定要可取，烘箱门不得关死，防止爆炸。中间观察时人不得面对烘箱开门，以防发生意外。
贮存于阴凉、通风的专用库房内，温度不超过30℃，远离火种和热源。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条