1) refractory concrete
耐火混凝土
1.
Facts prove that the new refractory concrete lining is superior to the traditional firebricks lining in construction, price as well as in application.
阐述了工业煤气发生炉耐火内衬以耐火混凝土替代耐火砖改造的工艺过程,对施工技术和材料做了详细介绍,并对改造后的使用过程进行了综合分析。
2.
The furnace top with refractory concrete is an important part of phosphorus furnace, which is as main equipment in yellow phosphorus production .
制磷电炉是黄磷生产装置的关键设备 ,耐火混凝土炉顶是电炉的重要组成部分 ,介绍炉顶结构特点和技术要求。
3.
The development situation, categories and performance of refractory concrete have been introduced and the method for mix proportion design of refractory concrete has been established.
本文以研究钢结构用混凝土防火保护层为目的，介绍了耐火混凝土的发展概况、分类和性能，确立耐火混凝土配合比设计的方法。
2) fireproof concrete
耐火混凝土
1.
Fireproof concrete not only can be taken the place of slag iron,but also the cost is lower and use life is longer.
用耐火混凝土挡渣墙可以代替挡渣铁,且费用低,使用寿命长。
3) fire resistent concret casting
耐火混凝土浇注
4) siliceous refractory concrete
硅质耐火混凝土
5) high temperature resisting refractory concrete
高温耐火混凝土
6) refractory insulating concrete
耐火隔热混凝土
补充资料：耐火混凝土
由耐火集料、粉料和胶结料加水或其他液体配制不经煅烧而直接使用的不定形耐火材料，也称耐火灌筑材料。它可分为：①普通耐火混凝土。所用集料有高铝质、粘土质、硅质、碱性材料(镁砂、铬铁矿、白云石等)或特种材料（碳素、碳化硅、锆英石等），也可以采用几种耐火集料组合。②隔热耐火混凝土。主要用耐火轻集料配制。所用轻集料有膨胀珍珠岩、蛭石、陶粒、多孔粘土熟料、空心氧化铝球等，也可用几种耐火轻集料组合，或与耐火集料共同组合。耐火混凝土所用胶结料有高铝水泥、磷酸盐胶结料、水玻璃胶结料、粘土等。
耐火混凝土为不烧制品，生产工艺简单，节省能源，可按照需要造型,整体性比砖砌炉衬好,适宜于机械化施工，合理利用时往往能延长炉衬寿命。耐火混凝土主要用于冶金、石油、化工、建筑材料、机械等工业窑炉中。一般使用温度为1300～1600°C。使用温度低于 900°C的耐火混凝土称为耐热混凝土，主要用于热工设备的基础、烟囱、烟道等构筑物中。
20世纪50年代以来，以耐火混凝土为主的不定形耐火材料发展迅速，在工业发达国家中已占耐火材料总产量的30～50％。中国从50年代以来，耐火混凝土已在各种工业窑炉中广泛应用。
参考书目
冶金工业部建筑研究总院：《耐火混凝土》，冶金工业出版社，北京，1980。
耐火混凝土为不烧制品，生产工艺简单，节省能源，可按照需要造型,整体性比砖砌炉衬好,适宜于机械化施工，合理利用时往往能延长炉衬寿命。耐火混凝土主要用于冶金、石油、化工、建筑材料、机械等工业窑炉中。一般使用温度为1300～1600°C。使用温度低于 900°C的耐火混凝土称为耐热混凝土，主要用于热工设备的基础、烟囱、烟道等构筑物中。
20世纪50年代以来，以耐火混凝土为主的不定形耐火材料发展迅速，在工业发达国家中已占耐火材料总产量的30～50％。中国从50年代以来，耐火混凝土已在各种工业窑炉中广泛应用。
参考书目
冶金工业部建筑研究总院：《耐火混凝土》，冶金工业出版社，北京，1980。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。