1) covulcanization
共硫化性
1.
The results showed that the CR/CIIR blend with better covulcanization was obtained by using ZnO/sulfur curing system;and a CR/CIIR blend with better comprehensive physical properties was obtained when CR/CIIR with 80/20 blending ratio,40 phr carbon black N550 and 10 phr cumar resin were used.
结果表明,采用氧化锌/硫黄硫化体系的CR/CIIR并用胶共硫化性较好;当CR/CIIR并用比为80/20、补强剂为炭黑N550(用量40份)、增塑剂为固体古马隆树脂(用量10份)时,并用胶的综合物理性能较好。
2) co-curing agent
共硫化剂
3) Co-vulcanization
共硫化
1.
A new process,heat treatment-dynamic vulcanization,was found to be effective in improving the mechanical properties and co-vulcanization of the NR/EPDM blend.
采用了一种新的工艺方法──热处理－动态硫化法，有效地改善了ＮＲ／ＥＰＤＭ并用胶的共硫化性和力学性能。
4) Ethoxylated coconut oil fatty acid monoethanolamide
共硫酸化
5) vulcanized blend
硫化共混物
6) curing characteristic
硫化特性
1.
The differences of thermooxiadative stability,curing characteristic and mechanical properties of hydrogenated nitrile rubber(HNBR) with different degree of hydrogenation were disscussed.
考察了丁腈橡胶(NBR)氢化过程中聚丁二烯的顺式-1,4-结构、反式-1,4-结构及乙烯基微观结构的变化,讨论了不同氢化度的氢化丁腈橡胶(HNBR)的热氧化稳定性、硫化特性和力学性能的差异。
2.
In this paper,the influence of the ratio of the CR/PUR blends on the curing characteristic,mechanical property,hot ageing resistance and thermo compression set of the blends were studied.
研究了共混比对氯丁橡胶/聚氨酯橡胶(CR/PUR)的硫化特性,硫化胶力学性能、耐热老化性能以及高温压缩永久变形的影响。
3.
The results showed that the two types of BR had similar thermostability and curing characteristics.
结果表明:两者的热稳定性相近,具有相似的硫化特性;BR9002L的耐机械降解性能稍好于BR9000;但BR9002L具有较小的相对分子质量、较窄的相对分子质量分布、较好的加工流动性、较严重的冷流性和较长的门尼焦烧时间。