1) synergistic accelerated corrosion test
循环加速腐蚀试验
1.
By means of synergistic accelerated corrosion test and electrochemical measuring,the corrosion behavior of copper-stainless steel composites and Cu in HSO_(3)~(-)/Cl~- media was studied.
通过循环加速腐蚀试验和电化学测试方法,研究了3种铜-不锈钢复合材料和纯铜在HSO3-和/或Cl-介质中的腐蚀行为。
2) Immersion-wet-dry cycle accelerated corrosion test
浸渍干湿循环加速腐蚀试验
3) cyclic corrosion test
循环腐蚀试验
1.
By use of solventborne coatings and waterborne coatings,the influence of NORSOK M-501 cyclic corrosion test,ASTM B117 salt spray test,ASTM 5894 cyclic corrosion test and ASTM 5894 salt spray test on coatings have been studied.
分别采用溶剂型涂料和水性涂料体系,考察了NORSOK M-501循环腐蚀试验、ASTM B117盐雾试验、ASTM 5894循环腐蚀试验和单独的ASTM 5894盐雾试验对涂层的影响。
4) corrosion cycle test
腐蚀循环试验
5) accelerated corrosion test
加速腐蚀试验
1.
With measuring and analyzing corrosion morphology,potential and EIS,the initial corrosion of aluminum alloys in marine atmosphere and correlation of simulated marine atmosphere accelerated corrosion test and outfield corrosion test were studied.
通过对模拟海洋大气加速腐蚀试验和外场暴露试验中的LY12铝合金初期腐蚀形貌、电位和交流阻抗等的测量和分析,研究铝合金在海洋大气环境下的初期腐蚀行为,并考察加速腐蚀试验结果和外场暴露试验结果的相关性。
2.
Usually,corrosion resistance of weathering steels is evaluated by the weight-loss method in an accelerated corrosion test.
通常利用加速腐蚀试验采用失重法表征耐候钢的耐大气腐蚀性能。
3.
The corrosion behavior of typical high-strength aluminum alloy LC4 was studied by accelerated corrosion tests of cyclic wet-dry intermittent immersion designed to simulated industrially polluted atmospheric environment,and corrosion mechanism was also discussed.
通过干湿周浸循环加速腐蚀试验,用NaHSO3和NaCl分别模拟对大气腐蚀有明显影响的两种大气污染组分SO2和Cl-。
6) accelerated corrosion experiment
加速腐蚀试验
1.
Using electrochemistry experiment,salt spray tests and accelerated corrosion experiment,under the ocean atmospheric corrosion and the polluted air corrosion environment,the corrosion behavior of different composition of hot-dip Zn-Mg alloy coated steel sheet was studied.
通过电化学试验、盐雾加速试验和全浸加速腐蚀试验,在模拟海洋性大气腐蚀环境和工业与重污染大气腐蚀环境条件下,研究了不同化学组成的钢基表面热镀Zn-Mg合金镀层的腐蚀行为。
2.
After having been corroded by seawater in accelerated corrosion experiment, based on rule and cause of changes of strength and weight loss rate, experiment data has been provided for quantitative analysis of broken state.
60范围内的混凝土试件,采用加速腐蚀试验研究了在海水侵蚀后,其强度、重量损失随时间变化的规律及原因,并为试件损伤状态定量化解析提供了试验数据。
3.
After having been corroded by seawater in accelerated corrosion experiment,basing on rule and cause of changes of strength and weight loss rate,experimental data has been provided for quantitative analysis of broken state.
采用普通硅酸盐水泥和矿渣硅酸盐水泥,分别配制了水灰比在0 45～0 60范围内的混凝土试件,采用加速腐蚀试验研究了在海水侵蚀后,其强度、重量损失随时间变化的规律及原因,并为试件损伤状态定量化解析提供了试验数据。
补充资料：大气加速老化试验
分子式：
CAS号：
性质：又称大气加速老化试验。将胶黏剂胶接的试样置于能整天跟踪太阳的自动暴晒试验机上，使其始终受到比自然暴晒时强得多的光照，进行短时间试验后测定其性能变化。
CAS号：
性质：又称大气加速老化试验。将胶黏剂胶接的试样置于能整天跟踪太阳的自动暴晒试验机上，使其始终受到比自然暴晒时强得多的光照，进行短时间试验后测定其性能变化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条