1) MgO whiskers
MgO晶须
1.
MgO whiskers were obtained on the surfaces of pressed specimens composed of MgO-Al materials treated at 1500℃ for 6h under controlled atmosphere.
采用适当MgO Al比例物料,压制成型后放入气氛炉中于1500℃烧制6h,最终在样块表面得到MgO晶须。
2.
The thermodynamics conditions of the preparation of MgO whiskers were given.
本文用热力学计算了C还原MgO在不同温度下平衡时Mg的分压，并计算给出生成MgO晶须的热力学条件。
3.
With their high melting point, great intensity and high elastic strength, MgO whiskers have been developed as an intensifier used in many composites.
MgO晶须具有熔点高、强度大和弹性模量高等性能优点,制备工艺和设备简单,且成本低,很适合作为多种复合材料的强化材料,因此,研究氧化镁晶须的生长条件和生长机理有着十分重要的意义。
2) whisker
[英]['wɪskə(r)] [美]['wɪskɚ]
晶须;触须
3) magnesium oxide nanocrystallite
MgO纳米晶
4) MgO cryslal
MgO晶体
5) MgO crystal
结晶MgO
6) Single Crystal MgO
单晶MgO
1.
Study on High Quality Surface Protection of Single Crystal MgO Polishing Substrate;
单晶MgO抛光基片高质量表面保护研究
2.
Single crystal MgO has excellent performances such as excellent thermal stability,optical characteristic,electrical insulativity, chemical stability and mechanical properties.
单晶MgO具有超高的耐温性，其透光率、热导率、电绝缘性、化学稳定性和机械强度等方面性能优异。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。