1) aluminide coating
铝化物涂层
1.
High-temperature oxidation life of aluminide coating on Co-base superalloy;
钴基超合金铝化物涂层的高温氧化寿命
2.
High temperature oxidation behavior for aluminide coating on the single crystal superalloy containing rhenium;
含铼单晶高温合金铝化物涂层的高温氧化行为
3.
The development of aluminium alloys and aluminide coatings is reviewed.
综合国内外铝合金及铝化物涂层的发展,较全面地介绍了涂层类型、制备方法及应用。
2) aluminide micro-crystalline coating
铝化物微晶涂层
1.
The oxidation results conducted in air at 1000℃for 100h show that the aluminide micro-crystalline coatings exhibited superior oxidation resistance and improved the adhesion of oxide scales greatly.
采用新型高频电脉冲沉积技术在１Ｃｒ１８Ｎｉ９Ｔｉ不锈钢表面上获得了晶粒尺寸约为几十到几百纳米的微晶铝化物涂层在１０００℃空气中恒温氧化１００ｈ的实验结果表明：获得的铝化物微晶涂层具有优异的抗高温氧化性能，而且显著提高了氧化膜的抗剥落能力。
3) Al-modified silicide coating
铝改性硅化物涂层
1.
Structure of Al-modified silicide coatings on a Nb-based ultrahigh temperature alloy by pack cementation process;
铌基超高温合金包埋渗铝改性硅化物涂层结构
4) alumina coating
氧化铝涂层
1.
An alumina coating with a thickness of 100μm on a titanium substrate was prepared by cathodic micro-arc electrodeposition.
采用阴极微弧电沉积在钛表面生成了厚度达100μm的氧化铝涂层,研究了不同电压下涂层的结构和组成,分析了涂层的生长规律和形成过程。
2.
Results indicate that an alumina coating with a thickness of about 40nm can be obtained on the aluminum borate whiskers.
结果表明 :试验采用的涂覆工艺可以在硼酸铝晶须表面获得 40 nm厚的氧化铝涂层。
5) alumina coat
氧化铝涂层
1.
Palladium catalyst for selective hydrogenation C_3 cut, supported on porous ceramics modified by alumina coat , was prepared.
采用氧化铝涂层改性后的多孔陶瓷为载体,制备以钯为活性组分的C3馏分选择性加氢催化剂。
6) aluminium/alumina film
铝/氧化铝涂层
补充资料：铝化物涂层
分子式：
CAS号：
性质：以铝为主要组元的一类扩散型抗高温氧化无机涂层体系。涂层结构大致分为三层:最外层是结构致密的氧化铝膜，中间层是铝与金属基体形成的金属间化合物，内层为扩散进入少量铝原子的基体层。涂层中往往还加入铬、硅、锰和稀土类元素进一步改善抗氧化性能，涂覆方法有包埋渗涂、料浆喷涂、热浸渗涂、等离子喷涂和物理气相沉积等。
CAS号：
性质：以铝为主要组元的一类扩散型抗高温氧化无机涂层体系。涂层结构大致分为三层:最外层是结构致密的氧化铝膜，中间层是铝与金属基体形成的金属间化合物，内层为扩散进入少量铝原子的基体层。涂层中往往还加入铬、硅、锰和稀土类元素进一步改善抗氧化性能，涂覆方法有包埋渗涂、料浆喷涂、热浸渗涂、等离子喷涂和物理气相沉积等。