2) electrochromism
电致变色性
1.
The results showed that that when mole ratio between aniline and anisidine is 2 ∶1,better reaction conditions of synthesizing polyaniline-co-o-anthranilic with good solubility,electrochromism and high yield is as follows: acid c.
得出在苯胺与邻胺基苯甲酸摩尔分数为2∶1时,制得溶解性和电致变色性都很好且产率较高的聚苯胺-邻胺基苯甲酸的较佳反应条件为:盐酸浓度为1。
2.
Its electrochromism capability is studied in different acidity medium.
4mol·dm-3,苯胺与邻甲氧基苯胺的摩尔配比为 3∶1的条件下合成了聚苯胺-邻甲氧基苯胺,对其在不同酸度介质的电致变色性能进行了研究,结果表明在 0。
3.
Poly(aniline-co-o-anisidine) have good electrochromism .
邻甲氧基苯胺与苯胺共聚能有效提高聚苯胺的溶解性和可加工性 ,所得的聚苯胺 -邻甲氧基苯胺具有很好的电致变色性。
3) Photochromic character
先致变色性能
6) electrochromic
电致变色
1.
Synthesis and characterization of PANI/PSSA-PVA electrochromic film;
聚苯胺/聚苯乙烯磺酸-聚乙烯醇电致变色膜的制备和表征
2.
Properties of electrochromic MoO_3 thin films on plastic substrate;
塑料基MoO_3电致变色薄膜性能
3.
The electrochromic effect of LiClO_4 polyelectrolyte;
LiClO_4有机高分子电解质的电致变色效应
补充资料：氧化钨电致变色陶瓷
分子式： WO3
CAS号：
性质：含钨阴极着色电致变色材料。氧化钨的多晶和非晶结构均具有电致变色性能。变色效应随晶粒尺寸减小而增强。可在碱金属离子导体的电解质中着色与漂白，变色反应为WO3(漂白态)+xM++xe-→MxWO3(着色态)。多晶氧化钨薄膜的调制范围在红外区，非晶薄膜的调制范围在可见光与近红外区，漂白态为透明状态，着色态为蓝色。采用溅射、化学气相沉积等方法制备。用于机敏窗口材料和大屏幕显示。
CAS号：
性质：含钨阴极着色电致变色材料。氧化钨的多晶和非晶结构均具有电致变色性能。变色效应随晶粒尺寸减小而增强。可在碱金属离子导体的电解质中着色与漂白，变色反应为WO3(漂白态)+xM++xe-→MxWO3(着色态)。多晶氧化钨薄膜的调制范围在红外区，非晶薄膜的调制范围在可见光与近红外区，漂白态为透明状态，着色态为蓝色。采用溅射、化学气相沉积等方法制备。用于机敏窗口材料和大屏幕显示。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。