1) sodium polymethylacrylate
聚甲基丙烯酸钠
1.
In order to lower the gels in the polymerization of elastic acrylate emulsion, sodium polymethylacrylate (PMANa) is used as protective colloid of acrylate emulsion.
为了降低高固含量弹性丙烯酸酯乳液聚合的凝聚率,选择了聚甲基丙烯酸钠作为丙烯酸酯乳液聚合的保护胶体,研究了其用量对乳液聚合和乳液性能的影响,探讨了它对丙烯酸酯乳液的稳定机理。
2) sodium methylacrylsulfonate
甲基丙烯磺酸钠
1.
The grafted copolymer of St-SMAS was synthesized by graft copolymerization of starch with sodium methylacrylsulfonate(SMAS).
以淀粉、甲基丙烯磺酸钠(SMAS)为主要原料,通过接枝共聚反应,合成了淀粉/甲基丙烯磺酸钠接枝共聚物(St-SMAS)。
2.
A polyether grafted copolymer of acrylic acid/sodium methylacrylsulfonate,which can be used as superplasticizer,was prepared by water solution polymerization using acrylic acid,sodium methylacrylsulfonate and acrylic acid-polyoxyethylene ester as monomers and ammonium persulfate as initiator.
以丙烯酸、甲基丙烯磺酸钠和丙烯酸聚氧乙烯酯为单体、过硫酸铵为引发剂,经水溶液聚合制备了可用作聚羧酸盐高效减水剂的聚醚接枝丙烯酸/甲基丙烯磺酸钠共聚物。
3.
new and practical coulometric methodwas developed to determine the content ofsodium methylacrylsulfonate ,the third com-ponent in the polymerizing mixture of poly-acrylonitrile.
本文首次提出了用库仑滴定法测定腈纶聚合原料混合液中甲基丙烯磺酸钠的含量，解决了腈纶生产中染色性能控制问题之一。
3) sodium methyl acryl sulfonate
甲基丙烯磺酸钠
1.
Terpolymer of sodium methyl acryl sulfonate-N,N-dimethylacrylamide-acrylamide(SMAS-DMAM-AM)was synthesized by terpolymerization in aqueous solution.
采用甲基丙烯磺酸钠(SMAS)、N,N-二甲基丙烯酰胺(DMAM)、丙烯酰胺(AM)为原料合成耐温抗盐驱油共聚物,研究影响共聚反应的各种因素和变化规律,讨论功能性单体的种类和含量对共聚物性能的影响,确定合理的聚合工艺条件。
2.
Enhanced oil recovery(EOR)performances of heat resistant and salt tolerant terpolymer of sodium methyl acryl sulfonate-N,N-dimethylacrylamide-acrylamide(SMAS-DMAM-AM)were determined in simulated oil well water solution.
系统测定了甲基丙烯磺酸钠-N,N-二甲基丙烯酰胺-丙烯酰胺(SMAS-DMAM-AM)三元共聚物在驱油条件下的各项性能;研究了在高温、高盐地质条件下表观粘度的影响因素及变化规律。
4) sodium methacrylate
甲基丙烯酸钠
1.
Fracture behavior of ethylene-vinyl acetate vulcanizates reinforced by sodium methacrylate or high abrasion furnace black;
甲基丙烯酸钠和高耐磨炭黑增强乙烯-乙酸乙烯酯橡胶的断裂行为
2.
Reinforcement of EVA by sodium methacrylate prepared in situ;
原位生成甲基丙烯酸钠补强EVA的研究
3.
The study of EVM vulcanizates reinforced by in situ prepared sodium methacrylate;
原位生成甲基丙烯酸钠增强EVM硫化胶的性能
5) sodium salt of methacrylic acid
甲基丙烯酸钠盐
1.
A soap-free poly(styrene/butylacrylate) P (St/BA) emulsion was prepared in the presence of the sodium salt of methacrylic acid.
在少量甲基丙烯酸钠盐的存在下,成功合成了具有高稳定性、高透明性的聚(苯乙烯/丙烯酸丁酯)P(St/BA)无皂共聚乳液。
6) poly(sodium acrylate and 2-acrylamido-2-methylpropanesulfonic acid)
聚(丙烯酸钠/2-丙烯酰胺基-2-甲基丙磺酸)
补充资料：甲基丙烯酸钠
分子量： 108
中文名称：甲基丙烯酸钠；甲基丙烯酸钠盐
理化特性：白色超细粉末，比重：0.3。溶解于水，溶液纯清透明。
产品质量：
含量： ≥99%
水份： ≤3000ppm
溶点： ≥300℃
PH： 7-8%
说明：补充资料仅用于学习参考，请勿用于其它任何用途。