1)  TiNiCu shape memory alloy
TiNiCu记忆合金
1.
TiNiCu shape memory alloy samples were amorphized by 400keV Xe~+ ions at room temperature using IVEM-Tandem Facility at Argonne National Laboratory.
　TiNiCu记忆合金在美国Argonne国家实验室IVEM TandemNationalFacility加速器产生的400keVXe+离子辐照到0。
2)  Ti
Ti
1.
EAM CALCULATION OF FORMATION ENTHALPIES OF Al,Li AND Mg(Ti) INTERMETALLIC COMPOUNDS;
Al-Li-Mg(Ti)合金形成焓的EAM研究
2.
ICP-AES Determination of Mn,Si,Al,Ti,Nb,La in Ultrahigh Strength Steel;
ICP-AES法测定超高强度钢中Mn,Si,Al,Ti,Nb,La杂质元素
3.
Synthesis of the Red Long Afterglow Phosphor Gd_2O_2S∶Eu, Mg, Ti by Microwave Radiation Method and Its Luminescent Properties;
微波法合成红色长余辉发光材料Gd_2O_2S∶Eu,Mg,Ti及其发光特性
3)  Ti+
Ti~+
4)  titanium
Ti
1.
Structure and High Temperature Tribological Behavior of Carbonaceous Mesophases Doped with Metallic Elements-titanium (Ti) and Nickel (Ni);
掺Ti/Ni碳质中间相的结构及其高温摩擦性能
2.
The microstructural evolution of a nickel-base single crystal superalloy with different content of titanium as-cast state and during prolonged aging at 1000℃ was investigated.
研究了不同Ti含量对一种镍基单晶高温合金的铸态组织以及在1000℃长期时效后的组织演化。
3.
The natural corrosion potential,corrosion rate and steady-state polarization curves of Q235B carbon steel,TA2 titanium and navel brass in seawater were measured.
测定了Q235B碳钢、TA2钛和海军黄铜在海水中的自然腐蚀电位、腐蚀速率和稳态极化曲线,测定了不同面积比时电偶对电偶电流的大小、方向,电偶电位以及电偶对阳极和阴极的失重速率,由电偶对不同面积比的数据得到Q235B碳钢被Ti电偶极化的动态极化曲线。
5)  Ti(Ⅳ)
Ti（）
6)  Ti(Ⅳ)
Ti（Ⅳ）
参考词条
补充资料：高温形状记忆合金
分子式：
CAS号：

性质：一般指高于普通形状记忆合金工作温度上限的形状记忆合金。高温形状记忆合金是在TiNi中加入Au，Pt或Pd取代Ni，用以提高相变点。其中有实用价值的是TiNi-Pd系。它有较高形状记忆应变(5％～6％)。随钯含量增加，形状恢复温度As最高可达到560℃。TiNi-Pd高温形状记忆合金的形状记忆效应机理与TiNi记忆合金类似，为热弹性马氏体相变时，相界/畴界作可逆运动，Ti50Nil3Pd37是TiNi-Pd系高温记忆合金的一种，形状恢复温度As为347℃，相变热滞为8℃，形状记忆应变为6％，室温和350℃断裂强度分别为1112MPa和918MPa。