1) mold pressing parameter
模压条件
1.
The influence of mold pressing parameters on electrical resistance of HDPD/CB composites;
模压条件对聚乙烯/碳黑PTC复合材料电阻特性的影响
2) autoclaved condition
蒸压条件
1.
the compressive strength of autoclaved waste glass lime system is studied by using XRD,SEM,IR and mechanical properties in different autoclaved conditions.
利用X射线衍射分析、扫描电子显微镜、红外光谱、力学性能等方法研究了不同蒸压条件下废玻璃石灰系统的强度。
3) decompression condition
负压条件
1.
It was showen that a certain decompression condition facilitated expulsion of the gas out of the PAA pores.
研究了模板组装过程不同压力条件对溶胶向模板孔洞中填充度的影响,发现在一定的负压条件下,有利于PAA孔中气体的排出,得到高的溶胶填充度,进而制备出高质量的纳米线阵列。
5) fusing condition
压烫条件
1.
How to control fusing conditions during the double point fusible interlining is used is particular.
同时对双点粘合衬在使用过程中的压烫条件的控制加以阐述 ,力求做到配伍的合理性和最佳性。
6) compacting conditions
压制条件
1.
In designing and developing deflection yoke core used for displays, not only the materials, the compacting conditions, and the sintering temperature, but also appropriate die should be considered so as to guarantee compacting dimensions.
设计显示器用偏转磁芯时,不但要考虑选用何种材料、生坯的压制条件及烧结温度,还必须依靠合适的模具保证成型尺寸。
补充资料：粉末冶金模压模工作零件的材料及技术要求
零件名称：
凹模芯棒
选用材料：
碳素工具钢：T10A，T12A
合金工具钢：GCr15，Cr12，Cr12Mo，Cr12W，Cr12MoV，9CrSi，CrWMn，CrW5
高速钢：W18Cr4V，W9Cr4V，W12Cr4V4Mo
硬质合金：钢结硬质合金，YG15，YG8（芯棒用硬质合金时，一般为钢与硬合金的焊接镶接形式）
热处理要求：
钢：60～63HRC
钢结硬质合金：64～72HRC
硬质合金：88～90HRA（钢的细长芯棒可降至55～58HRC，带接杆芯棒连接处局部35～40HRC）
其它技术要求：
1. 平磨后退磁
2. 粗糙度要求：
工作面：Rα 0.4～0.1μm
配合面及定位面：
Rα 1.6～0.4μm
非配合面：
Rα 3.2～1.6μm
3. 工作面及配合面公差等级：
IT5～IT7
零件名称：
模冲
选用材料：
碳素工具钢：T8A，T10A
合金工具钢：GCr15，Cr12，Cr12Mo，9CrSi，CrWMn，CrW5
热处理要求：
56～60HRC
其它技术要求：
1. 平磨后退磁
2. 粗糙度要求：
工作面：Rα 0.8～0.4μm
配合面及定位面：
Rα 0.4～0.1μm
非配合面：
Rα 3.2～0.8μm
3. 工作面及配合面公差等级：
IT5～IT7
说明：补充资料仅用于学习参考，请勿用于其它任何用途。