1) complex solid lubrication
复合固体润滑剂
1.
As the result, tribological properties of graded self lubrication composites were evidently improved with increasing content of CSL(complex solid lubrication), but excess content of CSL will lead to lower surface hardness of materials.
结果表明 :梯度自润滑复合材料随着复合固体润滑剂含量的增多 ,摩擦学性能明显改善 ,但润滑剂含量过高将导致材料表面硬度过低 ;该材料适用于高载荷下的润滑部件 ;脂润滑条件下 ,复合固体润滑剂与润滑脂结合在摩擦面上形成的膏状润滑膜使梯度自润滑复合材料的摩擦学性能显著改善 ;在脂润滑高载荷条件下 ,梯度自润滑复合材料的磨损主要发生在磨损初期 ,之后磨损极小 ,摩擦系数也趋于减
2) compasite sdid lubricating film
复合固体润滑膜
3) metal-solid lubricant composite material containing oil
金属-固体润滑剂复合含油材料
4) solid lubricant
固体润滑剂
1.
Mechanical properties and microstructure of Al_2O_3/TiC ceramics with the addition of solid lubricants;
添加固体润滑剂的Al_2O_3/TiC陶瓷材料力学性能和显微结构
2.
A solid lubricant OCL-RH for drilling fluid.;
钻井液用固体润滑剂OCL-RH的研制
3.
A kind of new anti-friction abrasion resistant coating is prepared with methyl methacrylate homopolymer as binder, MoS2 as solid lubricant, butadiene acrylonitrile rubber (BNR)/ acrylonitrile-butadiene-styrene (ABS) resin as flexibilizer, and other additives.
采用甲基丙烯酸甲酯均聚物为成膜物,以二硫化钼(MoS2)、丁腈橡胶/ABS树脂为固体润滑剂和增韧弹性体,加入其他助剂,获得一种新型的减阻耐磨涂料,并对其磨损机理进行了初步的探讨。
5) solid lubricants
固体润滑剂
1.
Self lubricating conducting composites with controllable phase transformation were prepared, which were added solid lubricants such as PTFE, graphite and Ekonal to the conductive matrix of LDPE/CB(carbon black).
研制了相变可控的复合导电和自润滑材料 ,它是以低密度聚乙烯 -炭黑为导电基材 ,加入固体润滑剂聚四氟乙烯、石墨和 Ekonal(聚苯酯的商品名 )构成。
2.
A novel high temperature composite based on Poly (phthalazinone ether sulfone ketone) (PPESK) adding solid lubricants and shot pitch-based carbon fibers are prepared in this paper.
以含二氮杂萘酮结构的聚醚砜酮（ＰＰＥＳＫ）树脂为基体，填加固体润滑剂和短炭纤维（ＣＦ）制备了新型耐热树脂基复合材料、研究了摩擦条件（如载荷、行程等）和ＣＦ含量对复合材料的摩擦磨损性能的影响，分析了ＰＰＥＳＫ树脂及其复合材料的磨损机理。
3.
The self lubricating mechanism of the composites was analyzed with emphasis on the effect of the solid lubricants.
采用粉末冶金自由烧结工艺制备出锡青铜基自润滑复合材料 ,对该类复合材料的力学性能与摩擦磨损特性进行了研究 ,从固体润滑剂角度就其室温与 45 0℃自润滑机理进行了分析与探讨 。
6) compound lubricant
复合润滑剂
补充资料：固体润滑剂
分子式：
分子量：
CAS号：
性质：用以润滑不能应用润滑油或润滑脂的机械摩擦部分的无机固体物质。种类很多，最重要的是石墨、二硫化钼和滑石粉。一氮化四硼的粉末（熔点2350℃），也可用作固体润滑剂的组分。固体润滑剂的粒子有晶体层格结构，可能互相滑过而发生润滑作用。主要用于负荷重、温度高的机械摩擦部分，如重轴承等。
分子量：
CAS号：
性质：用以润滑不能应用润滑油或润滑脂的机械摩擦部分的无机固体物质。种类很多，最重要的是石墨、二硫化钼和滑石粉。一氮化四硼的粉末（熔点2350℃），也可用作固体润滑剂的组分。固体润滑剂的粒子有晶体层格结构，可能互相滑过而发生润滑作用。主要用于负荷重、温度高的机械摩擦部分，如重轴承等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条