1) indirect zinc oxide
间接法氧化锌
1.
on its particle surface during vulcanization;the modulus at 300% and abrasion resistance of vulcanizate increased,and the compression set and compression fatigue temperature-rise decreased by using nano-zinc oxide instead of conventional indirect zinc oxide in equal weigh.
以纳米氧化锌等量替代普通间接法氧化锌 ,可提高硫化胶的 3 0 0 %定伸应力和耐磨性 ,减小压缩永久变形 ,降低压缩疲劳温升 ;以纳米氧化锌减量 5 0 %替代间接法氧化锌 ,仍可保证硫化胶的性能要求。
2.
The results showed that the Mooney viscosity of compound decreased,the Mooney scorch time extended and the curing behavior changed little by using nano-zinc oxide in reduced weight instead of indirect zinc oxide;the tear strength,abrasion resistance and H pull-out of vulcanizate increased;the endurance and average tread wear of test tire improved;and the cost of compound dereased.
用纳米氧化锌减量替代间接法氧化锌 ,胶料的门尼粘度下降 ,门尼焦烧时间延长 ,硫化特性基本保持不变 ;硫化胶的撕裂强度、耐磨性及H抽出力有所提高 ;试验轮胎的耐久性能及累计平均磨耗里程均较生产轮胎有所提高 ;可适当降低胶料成本。
3) Indirect-Oxidation process
间接氧化法
4) ZnO process
氧化锌法
5) indirect redox-titrimetry
间接氧化还原法
1.
The oxygen deficiency in the CexZr1-xO2-δ solid solution was determined by indirect redox-titrimetry after dissolving the solid sample in 3 mol/L sulphuric acid.
用3 mol/L硫酸溶液溶解样品,(NH4)2Fe(SO4)2作为还原剂,K2Cr2O7作为氧化剂,利用间接氧化还原法测定CexZr1-xO2-δ固溶体的氧缺陷值δ,方法的相对标准偏差为1。
6) indirect electro-oxidation
间接电氧化法
1.
2,3-Dimethoxy-5-methyl-1,4-benzoquinone was synthesized by indirect electro-oxidation.
采用间接电氧化法合成了2,3-二甲氧基-5-甲基-1,4-苯醌。
补充资料：间接法氧化锌
分子式：
CAS号：
性质： 以锌锭为原料制备的氧化锌，间接法氧化锌通常是将锌锭加热至1000℃熔融气化，再经氧气氧化而成。因锌锭纯度高，故间接法氧化锌的产品纯度高于直接法，氧化锌含量可高达99.0％～99.5％。
CAS号：
性质： 以锌锭为原料制备的氧化锌，间接法氧化锌通常是将锌锭加热至1000℃熔融气化，再经氧气氧化而成。因锌锭纯度高，故间接法氧化锌的产品纯度高于直接法，氧化锌含量可高达99.0％～99.5％。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条