1.
Poor solubility of C_(60) in water is one of the main obstacles which hinder the potential utilization of fullerene-containing materials.
富勒烯C60几乎不溶于水,从而阻碍了对富勒烯的进一步研究和应用。
2.
The inclusive compound of p-sulfonated calixarene with C_(60) is prepared and the product is charactered by UV-Vis spectra.
制备了杯[8]芳烃磺酸钠与C60的包合物,并利用紫外光谱对合成产物进行了表征。
3.
5% yield (based on consumed C_(60)) are:1∶3∶6 of molar ratio of C_(60),o-nitrobenzaldehyde and sarcosine,55℃ of reaction temperature,12 h of reaction time,40 mL of toluene solvent.
利用N-甲基甘氨酸、邻-硝基苯甲醛和C60反应,合成并分离出了含有硝基的新型富勒烯吡咯烷衍生物,通过正交试验对其工艺条件进行了研究,探讨了反应物剂量比、温度、时间和溶剂体积对产物产率的影响,得到了合成产物的最佳工艺条件:反应物剂量比为1∶3∶6、温度为55℃、反应时间为12 H、溶剂甲苯体积为40 ML,此时产物产率可达到53。
6) C 60
C60
1.
Ultraviolet Absorption Spectrum of Difference in Temperature(UVSDT) of C 60 was studied in different solvents by UV 240 ultraviolet visible spectrophotometer.
观测了C60 分子在乙醇、环己烷、正己烷、异丙醇等几种有机溶剂中吸光度随温度的变化。
2.
Being an electron deficient polyene, \ Fullerene (C 60) is prone to radical and nucleophilic addition reactions as well as to cycloadditions.
通过亚胺叶立德与C60 发生 1,3 偶极环加成反应的方法 ,合成了一种新的具有分子内给 受体系的C60吡咯烷衍生物 2 (4 ,5 二硫甲基 1,3 二硫环戊烯基 ) 3,4 富勒吡咯烷 (C66H9NS4) ,以红外、元素分析、核磁共振氢谱、紫外进行了表征 。
3.
This strategy was successfully applied to synthesize the first C 60-contained polyphosphazenes.
本文报道这种含叠氮基团的聚磷腈的合成 ,并以此合成连有 C60 基团的聚磷腈高分子 。