1) TCP/HA biphasic ceramic powder
β-TCP/HA双相陶瓷粉末
2) TCP/ HA biphase calcium phosphate powder
β-TCP/HA双相磷灰石粉末
3) porous HA/β-TCP biphasic bioceramic
多孔HA/β-TCP双相生物陶瓷
1.
Aimed at solving the problems on sintering of Ca-P bioceramics by using a conventional furnace, such as high sintering temperature, long holding time, large grain size and the difficulty to enhance the bioactive and the mechanical strength simultaneously, porous HA/β-TCP biphasic bioceramics were prepared by using a microwave plasma method.
针对常规马弗炉烧结钙磷生物陶瓷温度高、烧结时间长,制品晶粒粗、强度和生物学活性难于同时提高的问题,采用微波等离子体新技术烧结了多孔HA/β-TCP双相生物陶瓷。
4) porousβ-TCP/HA biphasic ceramic
多孔β-TCP/HA陶瓷
6) β-TCP ceramics
β-TCP陶瓷
1.
β-TCP ceramics have good biocompatibility and excellent osteoconductivity,as a kind of biodegradable substitute materials they are used widely for bone defect reparation in clinical.
传统β-TCP陶瓷材料的制备方法是将β-TCP及BG粉末按照一定的比例(通常4:1)直接混合,然后采用不同的方法成型后烧结而成。
补充资料：N,N′-双(β,β,β-三硝基乙基)乙二硝胺
分子式：
CAS号：
性质：白色针状结晶。溶于丙酮、硝基甲烷、二噁烷、乙酸甲酯、乙酸乙酯和热浓硝酸，微溶于甲醇、乙醇和醋酐，不溶于水、乙醚、苯、甲苯、氯仿、四氯化碳和二氯乙烷。密度1.87g/cm3。熔点179.2～180.5℃。耐强酸，对碱敏感。爆速8.97km/s(密度1.842g/Cm3时)；作功能力500ml(铅寿扩孔值)；撞击感度(10kg，25cm)100％；摩擦感度100％；爆发点232℃(5s)。108℃下第一个48h放气量为0.96ml/g(真空安定性)。先令乙二胺与甲醛的缩合液与硝仿的硝酸溶液反应，然后用硝硫混酸硝化上述反应产物制得。可用作传爆药。
CAS号：
性质：白色针状结晶。溶于丙酮、硝基甲烷、二噁烷、乙酸甲酯、乙酸乙酯和热浓硝酸，微溶于甲醇、乙醇和醋酐，不溶于水、乙醚、苯、甲苯、氯仿、四氯化碳和二氯乙烷。密度1.87g/cm3。熔点179.2～180.5℃。耐强酸，对碱敏感。爆速8.97km/s(密度1.842g/Cm3时)；作功能力500ml(铅寿扩孔值)；撞击感度(10kg，25cm)100％；摩擦感度100％；爆发点232℃(5s)。108℃下第一个48h放气量为0.96ml/g(真空安定性)。先令乙二胺与甲醛的缩合液与硝仿的硝酸溶液反应，然后用硝硫混酸硝化上述反应产物制得。可用作传爆药。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条