1) poly(ethylene 2,6-naphthalate)
聚2,6-萘二甲酸乙二酯
1.
Differential scanning calorimetry (DSC), X-ray diffraction, and nuclear magnetic resonance (NMR) were employed to study the influence of nucleating agent [1, 3: 2, 4-dibenzylidene sorbitol] (DBS)on the compatibility of the blend system-poly(ethylene terephthalate)/poly(ethylene 2,6-naphthalate) (PET/PEN).
用DSC、X-射线衍射、核磁共振、扫描电镜方法研究了成核剂1,3:2,4-二(亚苄基)-D山梨醇对聚对苯二甲酸乙二酯／聚2,6-萘二甲酸乙二酯共混体系(PET／PEN)相容性的影响。
2) DMN
聚2,6-萘二甲酸二乙酯
1.
Poly(ethylene terephthalate) (PET) and poly(ethylene 2, 6-naphthalate) (PEN) copolymers was prepared from DMT and DMN by means of copolycondensation, and the effects of the content of NCL and PEN on the properties of PET/PEN/NCL and its chips were studied.
用对苯二甲酸二甲酯(DMT)与2,6-萘二甲酸二甲酯(DMN)两种单体,共缩聚为聚对苯二甲酸二乙醇酯(PET)和聚2,6-萘二甲酸二乙酯(PEN)共聚物。
2.
Poly(ethylene terephthalate)(PET) and poly(ethylene 2, 6-naphthalate) (PEN) copolymer was synthesized from DMT and DMN.
采用对苯二甲酸二甲酯(DMT)与2,6-萘二甲酸二甲酯(DMN)合成了聚对苯二甲酸二乙酯(PET)和聚2,6-萘二甲酸二乙酯(PEN)共缩聚物,研究了PEN用量对共缩聚PET/PEN热性能的影响,并研究了采用PET/PEN制成的啤酒瓶的物理性能、气体阻隔性能和贮藏性。
3) poly(ethylene-2,6-naphthalenedicarboxylate)
聚2,6-萘二甲酸乙二醇酯
4) poly (ethylene2,6-napthalene dicarboxylate)
聚2,6-萘二酸乙二酯
5) Polyethylene naphthalate(PEN)
聚-2,6-萘二酸乙二醇酯(PEN)
6) BHEN
2,6-萘二甲酸乙二醇酯
补充资料：聚2,6-萘二甲酸乙二酯
分子式：
CAS号：
性质： 2,6-萘二甲酸与乙二醇缩聚制得的热塑性聚酯。结晶性聚合物。强度高，尺寸稳定性好，耐热、耐水、耐氨解，耐辐照和耐候性好。热变形温度91℃，玻璃化温度124℃，熔融温度273℃，连续使用温度155℃，较一般聚酯高，达F级。拉伸强度827MPa，弯曲模量2.55GPa。由2,6-二甲基萘催化氧化成萘二甲酸后与乙二醇高温高压缩聚制得。除熔融纺丝外，还可在280～300℃下挤塑并双轴拉伸成薄膜、注塑成不同制品。主要用作液晶材料、绝牡材料、磁带及胶片、特殊用包装材料等。
CAS号：
性质： 2,6-萘二甲酸与乙二醇缩聚制得的热塑性聚酯。结晶性聚合物。强度高，尺寸稳定性好，耐热、耐水、耐氨解，耐辐照和耐候性好。热变形温度91℃，玻璃化温度124℃，熔融温度273℃，连续使用温度155℃，较一般聚酯高，达F级。拉伸强度827MPa，弯曲模量2.55GPa。由2,6-二甲基萘催化氧化成萘二甲酸后与乙二醇高温高压缩聚制得。除熔融纺丝外，还可在280～300℃下挤塑并双轴拉伸成薄膜、注塑成不同制品。主要用作液晶材料、绝牡材料、磁带及胶片、特殊用包装材料等。