1) binder migration
胶粘剂迁移
1.
The main drives for binder migration were discussed in detail,which are capillary force and penetration pressure.
纸和纸板涂料的胶粘剂迁移影响涂布纸的最终质量。
2.
Binder migration during coating has serious effect on the quality of coated paper, the knowledge of the factors on migration and migration mechanism help to control binder migration effectively.
涂布加工过程中胶粘剂的迁移对涂布纸的质量有着重要的影响，掌握胶粘剂迁移的影响因素及迁移机理有助于对其进行有效的控制。
2) adhesive migration
胶粘剂的迁移
3) latex migration
胶乳迁移
4) Solvents permeating
溶剂迁移
5) adhesion and migration
粘附与迁移
6) adhesive
[英][əd'hi:sɪv] [美][əd'hisɪv]
胶粘剂
1.
Durability of polyurethane
adhesive in NaCl solution under load;
外力作用下聚氨酯胶粘剂在NaCl水溶液中的耐久性
2.
Working time forecast of
adhesive joints and its properties;
胶粘剂服役期与玻璃化温度以及吸水率关系的预测
3.
Design optimization for preparation process of organic montmorillonite modified epoxy resin adhesive;
有机蒙脱土改性环氧树脂胶粘剂的制备工艺优化设计
补充资料：1008a/b通用型环氧树脂胶粘剂
一、简介：
1008a/b系无溶剂室温快速固化型液态环氧树脂接着剂，固化后粘接强度大，收缩率低，固化物柔软性好，具有优良的电气性能及耐振动性。可作为电子元器件的通用型胶粘剂。
二、常规性能：
测试项目 测试方法或条件 1008a 1008b
外 观 目 测 黑色 棕褐色
密 度 25℃ g/cm3 1.1~1.3 1.1~1.3
粘 度 25℃ mpa·s 15000~25000 15000~25000
闪燃点 ℃ 170 150
保存期限 室温通风 一年 一年
三、使用工艺：
项 目 单位或条件 1008a/1008b
混合比例 重量比 100:100
可使用时间 100g,25℃，分钟 15
固化条件 ℃/hrs 25/12或60/1.5
四、用途：
1008a/b可作为电子元器件的通用型胶粘剂。
五、固化后特性：
项目 单位或条件 1008a/1008b
体积电阻率 25℃，ω·cm 4.3×1014
表面电阻率 25℃，ω 1.2×1014
绝缘强度 25℃，kv/mm >18
剪切强度 kgf/mm2 >200
拉伸强度 kgf/mm2 >130
冲击强度 kgf/mm2 >32
延伸率 % 100
六、贮存、运输及注意事项：
1．此类产品非危险品，按一般化学品贮运，产品贮存期见包装桶。
2．请看准所使用产品型号，然后对号入座；准确称量后，请充分搅拌均匀；称量大于100克，使用期会缩短。
3．被粘物品表面用化学溶剂（丙酮等）擦洗干净，特别光滑的被粘物最好能打毛处理，以提高粘接强度。
4．未用完的胶，要封盖严实，以防止水汽进入，影响使用效果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。