2) porous nickel plate
镍基多孔载体
3) porous nickel
多孔镍
1.
The experimental results indicated that the porous nickel deformed most severely when it was in situ oxidized and lithiated under loading.
熔融碳酸盐燃料电池在开始运行初期 ,承受一定负荷的多孔镍在转化为多孔氧化镍的过程中往往会受到较严重的形变破坏 ,对电池的使用性能和寿命造成不良影响。
2.
Analyze these parameters influence on the growth of porous nickel and obtain sediments porosity and relative density by ImageJ to find the optimal parameter.
采用喷射电沉积方法,分别选择不同的电流密度、喷射流量和两极间距及电沉积时间进行试验,分析了各试验参数变化对多孔镍形貌的影响规律,并用图形处理软件ImageJ对多孔镍的孔隙率和相对密度进行分析,找出了最佳试验参数。
3.
Pore structures of porous nickel samples prepared by powder metallurgic method are measured by MIP(mercury intrusion porosimetry),the porosity and the curve of pore diameter distribution are obtained.
用压汞法对用粉末冶金法制备的多孔镍试件进行了测试,得到了多孔镍试件的孔隙率及孔径分布曲线,并以Menger海绵体模型为基础,根据压汞实验数据确定了多孔镍试件的孔体积分形维数,发现多孔镍的孔隙结构具有明显的分形特征,分形维数在2。
5) Porous nickel electrode
多孔镍电极
6) porous skeleton
多孔基体
1.
The thermal energy storage phase change composite material with porous skeleton is presented.
本文提出了研制一种具有多孔基体的复合相变储能材料 ,通过实验分析了该储能材料的融解温度、融解热、热稳定性及微相结构等性能。
2.
The thermal energy storage material of building is prepared with the compound of expanded-perlite porous skeleton and organic-acid phase change materials by physical adsorption.
用膨胀珍珠岩多孔基体与有机羧酸进行物理复合,制备建筑储能材料,通过SEM分析了复合储能材料的微观结构,通过DSC测试其相变温度、相变焓。
补充资料：醚基多孔硅珠
分子式：
CAS号：
性质：一种二氧化硅胶。白色微珠形颗粒，以多孔硅珠为基料，经与三乙氧基γ-（β′-γ′环氧丙氧基）丙基硅烷反应制得。为高速液相色谱填料，用于分配色谱。
CAS号：
性质：一种二氧化硅胶。白色微珠形颗粒，以多孔硅珠为基料，经与三乙氧基γ-（β′-γ′环氧丙氧基）丙基硅烷反应制得。为高速液相色谱填料，用于分配色谱。