1) tungsten-based alloy
钨基合金材料
1.
The research status of tungsten-based alloys,including composition design and fabricating technology is summarized.
本文对钨基合金材料的研究现状,特别是对合金材料的成分设计及其制备工艺技术进行了综述,指出粉末原料的纳米化及添加晶粒长大抑制剂是制备高性能钨基合金材料的研究方向。
2) Tungsten alloy
钨合金材料
1.
Results show that under normal temperature and pressure conditions,this tungsten alloy materials have a longitudinal velocity ( c L) of 5.
利用两面顶压机和六面顶压机作为压力装置，分别对９３钨合金材料进行了高压超声测量。
2.
By using Co Kαand Fe Kαirradiations,the X-ray stress constants of tungsten alloys were determined with X-ray diffraction method.
以生产用的不同成分的钨合金材料加工成等强梁试样，用不同粒度砂纸磨削以模拟实际表面加工状态。
3) W/Cu Metal Matrix Composites
钨铜金属基复合材料
4) wha composites
钨合金复合材料
5) W matrix composite
钨基复合材料
1.
Microstructures and mechanical properties of nano-TiCp dispersion strengthened ultra-fine grained W matrix composite;
纳米TiC颗粒弥散增强超细晶钨基复合材料的组织结构与力学性能
6) Tungsten matrix composites
钨基复合材料
1.
In order to improve the mechanical properties of tungsten, tungsten matrix composites containing 0, 10%, 20%, 30% and 40%(vol) ZrC particles (ZrC/W composite), respectively, were prepared by vacuum hot pressing at 2000℃, 20MPa for 1h.
在 2 0 0 0℃、2 0MPa压力下 ,真空热压烧结 1h制备了ZrC颗粒含量分别为 0、10 %、2 0 %、30 %和 40 % (vol)的五种钨基复合材料 (ZrC/W)。
2.
The ablation properties of tungsten matrix composites reinforced by TiC and ZrC particles (two series of TiC p/W and ZrC p/W) were measured with an oxyacetylene ablation equipment.
用氧乙炔焰喷吹法对 Ti C和 Zr C增强钨基复合材料 ( Ti Cp/W和 Zr Cp/W两系列 )烧蚀性能进行了研究。
3.
The inner stress field in tungsten matrix composites can be shown through the finite element method.
对钨基复合材料内部应力场进行研究,结合钨基复合材料特有的组织结构建立数学模型,采用有限元数值计算的方法,利用有限元软件模拟钨基复合材料内部的应力场分布。
补充资料：高耐磨的碳化钨注渗钢基合金在塑料机械中的应用
碳化钨注渗钢基合金（下简称WCSA）技术，又名碳化钨——钢梯度耐磨材料制造技术。该技术已获得国家发明专利，具有自主知识产权。WCSA是采用高能离子注渗技术，在钢铁零部件表层内注渗进高耐磨的碳化钨（下简称WC），WC注渗层深度1.2-1.5mm，其中WC含量较多的富集层达到0.3-0.5mm。零部件表层获得WC“盔甲”后,硬度高，强韧性好,抗磨性能更好。WCSA应用于各种塑料机械中，使用寿命比目前塑料机械中常用的离子氮化层、堆焊或喷涂耐磨层、高合金工具钢、高速钢和不锈钢等材料制造成的零部件的使用寿命提高3-8倍，深受塑料机械制造商和塑料制品生产商的青睐。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。