1) silica fiber fabric
石英织物
1.
A 3dimensional silica fiber fabric reinforced silicon nitride composite was prepared by the polymer impregnation pyrolysis method using a preceramic polymer named perhydropolysilazane (PHPS) with the main backbone \_ n as precursor.
以分子结构单元为[Si H2NH]n的全氢聚硅氮烷作先驱体,采用聚合物浸渍裂解法制备了三维石英织物增强氮化硅基复合材料(3DSi O2f/Si3N4)。
2) quartz fabrics
石英纤维织物
1.
Advanced pedormance quartz fabrics from local supplier were developed for satisfying the items plan.
研制开发了国产高性能石英纤维织物。
3) astroquartz fabric
宇航石英织物
4) silica fabrics
矽石织物
5) asbestos web
石棉织物
6) quartz mineral
石英单矿物
1.
The results from X ray diffraction, scanning electron microscope and grain size analysis show that quartz minerals can be separated effectively from the loess samples by pyrosulfate (K 2S 2O 7) fusion hydrofluosilicic acid (H 2SiF 6) treatment.
X射线衍射分析、扫描电镜测试和粒度分析结果表明 ,用焦硫酸钾熔融 -氟硅酸溶解法可有效地分离黄土样中的石英单矿物 ,且提取后的石英颗粒形状和粒度组成没有明显受到化学反应影响。
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。