1) S(IB)S
聚苯乙烯-聚异戊二烯/丁二烯-聚苯乙烯三嵌段共聚物
2) styrene-isoprene-styrene block tercopolymer
苯乙烯-异戊二烯-苯乙烯三嵌段共聚物
1.
A hot-melt strippable coatings has been preparated by using styrene-isoprene-styrene block tercopolymer as film former and some supplementary materials.
选用合适组成及相对分子质量的苯乙烯-异戊二烯-苯乙烯三嵌段共聚物作成膜物质,添加某些辅助料,研制了一种热熔型可剥离涂料。
3) styrene-isoprene-styrene triblock copolymer
苯乙烯-异戊二烯-苯乙烯嵌段共聚物
1.
Toughening effect of styrene-isoprene-styrene triblock copolymer and its maleic anhydride grafted polymer on polystyrene/nano-CaCO_3 composites;
苯乙烯-异戊二烯-苯乙烯嵌段共聚物及其接枝马来酸酐增韧聚苯乙烯/纳米碳酸钙复合材料
4) styrene-butadiene-styrene ternary block copolymer
苯乙烯-丁二烯-苯乙烯三元嵌段共聚物
5) styrene-butadiene-styrene triblock copolymer
苯乙烯-丁二烯-苯乙烯三嵌段共聚物
1.
The styrene-butadiene-styrene triblock copolymer was modified by solution grafting copolymerization with maleic anhydride(MAH) and styrene (St) , then compounded with PS and CaCO_3 The effect of grafting modification of SBS on morphology and mechanical properties of PS/SBS-g-MAH/CaCO_3 ternary composites were investigated.
采用马来酸酐(MAH)和苯乙烯(St)作为接枝单体,通过溶液聚合法合成接枝极性基团的苯乙烯-丁二烯-苯乙烯三嵌段共聚物(SBS),然后与聚苯乙烯(PS)基体、碳酸钙(CaCO_3)粒子复合,用傅立叶红外光谱仪表征接枝处理前后SBS表面化学结构的变化;并研究了SBS改性对复合材料微观结构和力学性能的影响。
6) polystyrene-polyisoprere triblock copolymer
苯乙烯异戊二烯三元嵌段共聚物
补充资料：1,4-已二烯
分子式：C6H10
分子量：83.15
CAS号：592-45-0
性质：无色液体。熔点-138.7℃，沸点65℃，相对密度0.695（25/4℃），折光率1.4104，闪点-25℃。溶于苯、醇、醚。
制备方法：由乙烯和丁二烯经催化反应而得。乙烯和丁二烯在溶剂甲苯中反应，催化剂为氯化钴、氯化磷、三乙基铝，反应浊度为80-104℃，压力为3.92MPa。产品中除1,4-已二烯外，还含少量变，4-已二烯和碳八双烯类。
用途：用作乙丙胶的第三单体。
分子量：83.15
CAS号：592-45-0
性质：无色液体。熔点-138.7℃，沸点65℃，相对密度0.695（25/4℃），折光率1.4104，闪点-25℃。溶于苯、醇、醚。
制备方法：由乙烯和丁二烯经催化反应而得。乙烯和丁二烯在溶剂甲苯中反应，催化剂为氯化钴、氯化磷、三乙基铝，反应浊度为80-104℃，压力为3.92MPa。产品中除1,4-已二烯外，还含少量变，4-已二烯和碳八双烯类。
用途：用作乙丙胶的第三单体。