1) Latent curing agent
潜固化剂
1.
When this compound was added as a latent curing agent to single component moisture curable polyurethane system(SPU),bubbles of SPU formed during curing was obviously restrained.
将所合成的3-羟乙基-1,3-噁唑烷用作单组分湿固化聚氨酯体系的潜固化剂,抑泡效果明显,固化后样品的伸长率提高了10倍以上。
2) latent curing agent
潜在固化剂
3) curing agent
潜伏性固化剂
1.
Syntheses and properties of curing agent modified dicyandiamide by p-toluidine;
对甲苯胺改性双氰胺衍生物潜伏性固化剂的合成及性能
4) Latent curing agent PTSA
潜伏性固化剂PTSA
5) latent curing agent
潜伏性固化剂
1.
Study on latent curing agent of modified dicyandiamide for epoxy resin and its application;
改性双氰胺类环氧树脂潜伏性固化剂的研究及其应用
2.
Latent curing agents for one-component epoxy resin adhesives;
单组分环氧树脂胶粘剂用潜伏性固化剂
3.
A novel latent curing agent,poly(aryl ether ketone)/tris(salicylaldehydato)aluminium,wasused for curing epoxy resin.
本文提出一种新型潜伏性固化剂——聚芳醚酮/水杨醛铝,研究了这种固化体系引发环氧树脂固化的机理,固化剂对反应速度,固化物力学性能和电性能的影响,证明这种固化体系具有明显的潜伏效果,并能改善固化物的高温电性能。
6) Latent Curing Agents
潜伏型固化剂
补充资料：潜性固化剂
分子式：
CAS号：
性质：配制单组分环氧树脂胶黏剂时使用的固化剂。潜性固化剂与双酚A型环氧树脂及其他成分混合后，在室温下能贮存较长时间，但加热能起固化反应。潜性固化剂主要有如下几类：（1）双氰胺固化体系。双氰胺是传统的潜性固化剂，与树脂的混合物在室温下6个月以下是稳定的，但需160℃以上固化，为此发展了许多促进剂，较好的是脲衍生物（如3-苯基-1,1-二甲基脲、3-对氯苯基-1,1-二甲基脲等）、咪唑衍生物（如咪唑盐等），组成中温固化体系即120℃以上固化。（2）酰肼类。如已二酸二酰肼、壬二酸二酰肼、癸二酸二酰肼、间苯二甲酸二酰肼。（3）咪唑衍生物。（4）酸酐。（5）环氧树脂与胺加成物。（6）脲衍生物。（7）乙酰基丙酮盐。（8）BF3-胺络合物。（9）微胶囊潜性固化剂。
CAS号：
性质：配制单组分环氧树脂胶黏剂时使用的固化剂。潜性固化剂与双酚A型环氧树脂及其他成分混合后，在室温下能贮存较长时间，但加热能起固化反应。潜性固化剂主要有如下几类：（1）双氰胺固化体系。双氰胺是传统的潜性固化剂，与树脂的混合物在室温下6个月以下是稳定的，但需160℃以上固化，为此发展了许多促进剂，较好的是脲衍生物（如3-苯基-1,1-二甲基脲、3-对氯苯基-1,1-二甲基脲等）、咪唑衍生物（如咪唑盐等），组成中温固化体系即120℃以上固化。（2）酰肼类。如已二酸二酰肼、壬二酸二酰肼、癸二酸二酰肼、间苯二甲酸二酰肼。（3）咪唑衍生物。（4）酸酐。（5）环氧树脂与胺加成物。（6）脲衍生物。（7）乙酰基丙酮盐。（8）BF3-胺络合物。（9）微胶囊潜性固化剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。