1) mixed-valence copper
混合价铜
2) compound copper ore
混合铜矿
1.
Leaching of compound copper ore with NH 3·H 2O at normal atmosphere and high O 2 pressure has been studied.
对新疆某地的混合铜矿进行了常压氨浸和高氧压氨浸工艺研究 ,详细考察了NH3·H2 O浓度、铵盐用量、氧化剂用量、氧压、浸出温度、浸出时间等因素对浸出过程的影响。
2.
Extraction of compound copper ore using NH3· H2O under high-pressure O2 was studied.
对新疆某地混合铜矿采用高压氨浸工艺, 考了NH3·H2O浓度、NH4+盐用量、氧压、浸出温度、浸出时间及固液比等因素对浸出过程的影响。
3) mixed copper ores
混合铜矿石
4) copper-zinc bulk concentrate
铜锌混合矿
1.
A new leaching process for a low-grade copper-zinc bulk concentrate was studied.
研究了低品位多金属铜锌混合矿的浸出条件。
5) copper-bearing mixture
含铜混合液
1.
Hydrogen peroxide as oxidizer and sodium carbonate as remover, arsenic, iron, nickel, calciumand lead are removed from copper-bearing mixture by neutralization and precipitation, then use the liquor thathave been filtrated react with the sodium carbonate to produce basic copper carbonae and make the quality of theproduct meet the export request.
采用氧化和中和沉淀方法,以H_2O_2作氧化剂、Na_2CO_3作脱杂剂脱除含铜混合液中的As、Fe、Ni、Ca、Pb等杂质,利用其与碳酸钠反应生产减式碳酸铜,并使产品质量达到出口要求。
6) Mixed higher order cyanocuprate
混合高序铜
补充资料：混合价态
分子式：
CAS号：
性质： 又称价态起伏(valence fluctuation)。指在一些化合物中，金属离子的价态的不稳定性或组态间的波动。在一些稀土化合物体系中，例如硫化钐等，4fn与4fn-1d组态间的能量差很小，在一定的温度或压力下，电子可以在上述电子组态间迁移，电子迁移的时间小于10-11s，因而当利用穆斯保尔谱研究上述化合物时，只能观察到不同价态的平均效果。但由于光电子能谱的时间常数远小于电子的迁移时间，因而在光电子能谱中可以看到不同价态的分布状况。人们曾对稀土硫化物体系的价态波动进行了系统地研究。大多数稀土一硫化物具有金属性，表明稀土离子具有+3价，金属性来源于电子充填到离域的5d轨道构成的能带中。钐、铕和镱的一硫化物在常压下是绝缘体，磁性研究表明这些稀土离子的电子组态为f6，f7和f8。但在压力下，由于价态波动，这些化合物发生由绝缘体向金属的转变。
CAS号：
性质： 又称价态起伏(valence fluctuation)。指在一些化合物中，金属离子的价态的不稳定性或组态间的波动。在一些稀土化合物体系中，例如硫化钐等，4fn与4fn-1d组态间的能量差很小，在一定的温度或压力下，电子可以在上述电子组态间迁移，电子迁移的时间小于10-11s，因而当利用穆斯保尔谱研究上述化合物时，只能观察到不同价态的平均效果。但由于光电子能谱的时间常数远小于电子的迁移时间，因而在光电子能谱中可以看到不同价态的分布状况。人们曾对稀土硫化物体系的价态波动进行了系统地研究。大多数稀土一硫化物具有金属性，表明稀土离子具有+3价，金属性来源于电子充填到离域的5d轨道构成的能带中。钐、铕和镱的一硫化物在常压下是绝缘体，磁性研究表明这些稀土离子的电子组态为f6，f7和f8。但在压力下，由于价态波动，这些化合物发生由绝缘体向金属的转变。