1) unstable shear
失稳剪切
2) shear localization
剪切失稳
1.
Analysis of shear localization in void-containing materials;
含微孔材料的局部剪切失稳分析
3) adiabatic shear instability
绝热剪切失稳
1.
The join strength,penetration depth and condition of emerging adiabatic shear instability are discussed with single particle of uniform speed and different angle.
针对单个粒子相同入射速度不同入射角度的碰撞条件,探讨粒子与基体的结合强度、侵彻深度以及绝热剪切失稳的发生条件。
2.
The results indicated that the particles with higher effective plastic limit than that of substrate are easy to undergo adiabatic shear instability,while the substrate does not undergo adiabatic shear instability and releases deformation energy,which leads particles to rebound.
结果表明,与基板相比,有效塑性极限大于衬底的金属颗粒易发生绝热剪切失稳,此时,基板不发生失稳,并释放积攒的变形能,使颗粒发生回弹现象。
4) plastic shear instability
塑性剪切失稳
5) Thermoplastic Shear Instability
热塑剪切失稳
6) shear failure
剪切失效
1.
Shear failure is an important mode of dynamic failure of structural members under impulsive loading.
剪切失效是强动载荷作用下结构失效的重要模式 ,从自由梁在中点受到质量块撞击后发生剪切失效的无量纲判据的分析表明 ,在初始速度间断面上是否发生剪切失效取决于质量块无量纲初始动能、质量比及梁的无量纲厚
2.
Shear failure criterion was used to separate chips from workpiece.
在铣削模型二维等效简化的基础上,对高速切削仿真的关键技术进行了研究,用J-C模型建立工件材料模型,用剪切失效准则实现切屑和工件分离,切屑和刀具的接触摩擦模型采用修正的库仑摩擦定律,在ABAQUS软件中实现了对45钢的高速铣削仿真,对切削力和切屑温度场、应力场的仿真结果进行了分析,验证了有限元模型的合理性。
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。