1) heterogeneous precipitations method
非匀相沉淀
1.
Al2O3 coated Al composite ceramics were prepared by heterogeneous precipitations method and pressureless sintering.
采用非匀相沉淀法和常压烧结的方法制备出了Al2O3包裹Al复合陶瓷。
2) heterogeneous precipitation method
非匀相共沉淀
1.
BaTiO3 particles coated with CuO is prepared by the heterogeneous precipitation method,and MnO2 is added to improve the properties of the specimens.
为了提高边界层陶瓷电容器(GBBLC)的性能,采用非匀相共沉淀法制备了CuO包裹的BaTiO3粉体,并加入MnO2以改善样品的性能,按照普通电子陶瓷的制备工艺制得一系列样品,测试了样品的密度、体积收缩率,并研究了样品的显微结构。
2.
BaTiO_3 particles coated with CuO were prepared by the heterogeneous precipitation method, and B_2O_3 ,MgO were added to improve the properties of the specimens.
为了提高边界层陶瓷电容器(GBBLC)的性能,采用非匀相共沉淀法制备了包覆有CuO的BaTiO3粉体,加入B2O3、MgO以提高样品的性能,按照普通电子陶瓷的制备工艺制得一系列样品。
3) heterogeneous nucleation
非均匀沉淀
1.
Synthesis of coated-LiNi_(0.9)Co_(0.07)Mn_(0.03)O_2 cathode materials by heterogeneous nucleation
非均匀沉淀法包覆合成LiNi_(0.9)Co_(0.07)Mn_(0.03)O_2锂离子正极材料
4) heterogeneous precipitation
非均相沉淀
1.
Preparation of Fe-coated Si_3N_4 composite powder by heterogeneous precipitation-thermal reduction process;
采用非均相沉淀-热还原法制备铁包覆氮化硅复合粉末
2.
Preparation of nickel-coated Al_2O_3 spherical micro-powders by heterogeneous precipitation-thermal reduction process;
非均相沉淀热-还原法制备金属镍包裹氧化铝球形微粉
3.
The precursors for CoFe, CoNi, CoFeNi-coated alumina microspheres were synthesized by the heterogeneous precipitation route, respectively.
用非均相沉淀法制备了CoFe,CoNi,CoFeNi包裹氧化铝3种微球前驱体,在还原气氛中于720℃焙烧2h获得了包裹层颗粒分布均匀的纳米多元铁磁性合金/氧化铝复合微球。
5) homogeneous precipitation
均匀沉淀
1.
Study on pilot of Mg-Al-hydrotalcite preparation by using homogeneous precipitation;
均匀沉淀法制备镁铝水滑石的中试研究
2.
Study on preparation of Ag/TiO_2 film by homogeneous precipitation and its photocatalytic property;
均匀沉淀法制备载银TiO_2薄膜及其光催化性能的研究
3.
Synthesis and characterization of nano-ZnTiO_3 by homogeneous precipitation method;
均匀沉淀法合成纳米钛酸锌及其形态结构分析
6) heterogeneous precipitation method
非均相沉淀法
1.
Hollow glass microbeads were successfully coated by heterogeneous precipitation method,taking titanium sulfate solution as precursor and ammonia solution as precipitant,at 20 ℃ to 100 ℃ and pH value 3-9.
H2O为沉淀剂,在20~100℃、pH值为3~9的条件下,采用非均相沉淀法对空心玻璃微珠进行包覆。
2.
Al2O3/Ni nanocermets were prepared by the heterogeneous precipitation method and hot-pressing technique.
采用非均相沉淀法和热压工艺制备了Al2O3/Ni纳米金属陶瓷。