1) RTV block methyl silicone rubber
甲基嵌段室温硫化硅橡胶
1.
Main factors affecting vulcanization time of RTV block methyl silicone rubber.;
影响甲基嵌段室温硫化硅橡胶硫化时间的主要因素
2) methyl block RTV silicone rubber adhesive
嵌段甲基室温硫化硅橡胶黏合剂
3) Siloxanes and silicones,dimethyl hydroxy-terminated
室温硫化甲基硅橡胶(107型)
4) room-temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Enhancing methods of room-temperature vulcanized silicone rubber adhesive;
室温硫化硅橡胶胶粘剂的增强方法
2.
With PDMS(polydimethyl siloxane)of appropriate viscosity as matrix and addition of appropriate fillers and assistants,the room-temperature vulcanized silicone rubber coatings was successfully prepared.
采用一定粘度的聚二甲基硅氧烷为基体,加入适量填料和助剂,成功制备了室温硫化硅橡胶涂层。
3.
With hydroxyl group terminated PDMS on both side as feedstock, adding several kinds of fillers and adjuvants, the room-temperature vulcanized silicone rubber coatings are prepared.
以二羟基聚二甲基硅氧烷(PDMS)为基体,加入不同填料和助剂,制备了室温硫化硅橡胶涂层。
5) room temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Modified room temperature vulcanized silicone rubber adhesive filled in situ with silica white;
白炭黑原位填充的改性室温硫化硅橡胶胶黏剂
2.
Research progress in thermal conductive room temperature vulcanized silicone rubber;
导热室温硫化硅橡胶的研究进展
3.
Progress in reinforcemnet and modification of room temperature vulcanized silicone rubber;
室温硫化硅橡胶的增强改性研究进展
6) RTV silicone rubber
室温硫化硅橡胶
1.
Modification of RTV silicone rubber by nano-SiOx;
纳米SiOx改性室温硫化硅橡胶研究
2.
The structure and the surface characteristics of fumed silica and its application in HTV silicone rubber and RTV silicone rubber were introduced as well.
简述了气相法白炭黑的发展及国内生产情况 ,介绍了气相法白炭黑的结构和表面性质 ,以及在热硫化硅橡胶和室温硫化硅橡胶中的应用。
3.
The features and application of the operating agent for adjusting the rate of extrusion and the thixotropy of the compound, the thinner for improving the fluidity of the compound, and the plasticizer for regulating the hardness and the modulus of vulcanized compound used in RTV silicone rubber of condensed type were described.
介绍了缩合型室温硫化硅橡胶中常用的调节胶料挤出速度及触变性的施工助剂、改善胶料流动性的稀释剂、调节胶料硫化后硬度及模量的增塑剂的特点和作用。
补充资料:嵌段甲基室温硫化硅橡胶黏合剂
分子式:
CAS号:
性质:硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa,相对伸长率200%~500%,使用温度范围-60~200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7:3或5:5的比例混合配制成胶料,配制时也可加入适量的气相法白炭黑。使用前,加入0.5%~2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应,提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。
CAS号:
性质:硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa,相对伸长率200%~500%,使用温度范围-60~200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7:3或5:5的比例混合配制成胶料,配制时也可加入适量的气相法白炭黑。使用前,加入0.5%~2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应,提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。