1) element and microhardness distribution
元素和硬度分布
2) hardness of the element
元素硬度
3) Hardness Distribution
硬度分布
1.
The weld characteristics of 5A05 aluminum alloy by friction stir welding,such as the mechanical properties,microstructures and the hardness distribution have been introduced in the paper.
硬度试验表明:搅拌摩擦焊焊接接头的硬度分布存在一定的规律,即焊核区的硬度分布近似为均值,由中心向两侧,硬度值逐渐降低,当达到HAZ时,硬度达到最低值,然后其值逐渐增加,最终达到与母材同等水平。
2.
The hardness distribution without obviously declining gradient in one range of the hardened layer produced by plasma quenching is rather different from that by conventional quenching.
等离子表面淬火硬化层的硬度分布 ,在某一区域内无明显的硬度梯度 ,这与常规淬火方法的结果不太一样。
3.
This paper investigates the microstructure and hardness distribution of 40Cr steel produced by broad beam laser hardening.
对４０Ｃｒ钢宽带激光淬火组织和硬度分布进行了较细致的研究，结果表明，激光淬火区组织结构和硬度沿层深明显变化，淬火区中奥氏体呈薄膜状，不连续地分布于马氏体间。
5) Element distribution
元素分布
1.
Effect of pulse electric field on the solidification microstructure and element distribution of carbon steel;
脉冲电场处理对钢的凝固组织和元素分布的影响
2.
The microstructure and element distribution of AZ80 magnesium alloy as-cast and after solution and aging treatment were observed and analyzed by field emission scanning electron microscope(FESEM),energy dispersive spectrometer(EDS) and X-ray diffraction(XRD).
采用场发射扫描电镜(FESEM)、能谱(EDS)及X射线衍射(XRD)对AZ80镁合金铸态及经固溶、时效处理后的显微组织、主要元素分布进行了观察和分析。
3.
Accompanied with the spark discharge,the cell voltage presents oscillations within the range of several volts,and the surface morphologies,the element distribution as well as the surface potential distributions of the anodic layer are significantly changed.
在电火花的影响下,镁合金氧化试样的表面形貌、元素分布以及表面电位分布等都发生了显著的变化。
6) elements distribution
元素分布
1.
The elements distribution characteristics in the interfacial transition zone between lightweight aggregate and cement paste were studied by backscattered electron imaging and EDXA.
研究了高强页岩陶粒与水泥石及其界面区的元素分布特征,探测出界面区宽度约为20~30μm,研究表明界面区Ca2+向轻集料方向迁移、轻集料内水分向界面区扩散,结果使得界面区的硅钙比较基体小,结构较基体密实,显微硬度较基体大;分析了粉煤灰、矿渣对两相界面组成、结构与性能的影响规律,结果表明随着粉煤灰、矿渣的掺入,界面区硅钙比增大,界面区水泥石的孔隙率和平均孔径显著降低,显微硬度提高,界面得到增强。
2.
Based on the observation of SEM and EDXA technologies,the investigation on the micro-structural properties and the elements distributional characteristics of Interfacial Transition Zone(ITZ)of recycled concrete is conducted.
界面过渡区内外的元素分布规律存在着较大的差异,Ca、Si等元素在界面过渡区内出现了一定程度的聚集,在界面过渡区外的分布则较为连续。
补充资料：工程塑料硬度的检测--巴氏硬度计
HBa-1巴 氏 硬 度 计巴柯尔 (Barcol) 硬度 ( 简称巴氏硬度 ) 最早由美国 Barber-Colman 公司提出，是近代国际上广泛采用的一种硬度门 类，以特定压头在标准弹簧的压力作用下压入试样，以压痕的深浅表征试样的硬度。巴柯尔硬度计（巴氏硬度计）作为 专门测量玻璃钢制品、增强或非增强硬塑料、铝及铝合金、黄铜、紫铜等较软金属硬度的专用检测工具 （ 特别 适用于玻璃钢制品 ），已被大多数国家或国际组织认可。美国材料试验协会（ ASTM ）、日本工业规范（ JIS ）、中国等国家相继制定 《用巴柯尔硬度计测量玻璃钢（ GRP ）硬度试验方法》,《纤维增强塑料巴氏（巴柯尔）硬度试验方法》GB/T3854-1983 的国家标准。因此，巴柯尔硬度计是各生产单位、计量部门在质量认证、质量监控、计量测试等方面首选的专用检测仪器。 无锡市计量科学研究所，是我国制定巴柯尔硬度检定标准的主要参与者、巴柯尔硬度最高标准器的拥有者和国产第一台巴柯尔硬度计的研制和生产单位，也是国家实验室认证的巴柯尔硬度计专业检测机构。经过二十多年的不断完善，本所生产的 H Ba 系列巴柯尔硬度计的各项性能和技术指标完全与美国 Barber-colman 公司 GYZJ 系列硬度计相媲美 。